Degradation of bending properties of flax fiber reinforced polymer after natural aging and accelerated aging

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24620%2F20%3A00007013" target="_blank" >RIV/46747885:24620/20:00007013 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/abs/pii/S0950061819333628?via=ihub" target="_blank" >https://www.sciencedirect.com/science/article/abs/pii/S0950061819333628?via=ihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.conbuildmat.2019.117909" target="_blank" >10.1016/j.conbuildmat.2019.117909</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Degradation of bending properties of flax fiber reinforced polymer after natural aging and accelerated aging

Popis výsledku v původním jazyce

In this paper, the effect of natural aging and accelerated aging on the bending properties of flax fiber reinforced polymer (FFRP) is studied. Test results show that the flexural strength decreases by 11.2%, 14.9%, 15.5%, and the flexural modulus decreases by 21.3%, 32.3%, 35.8%, after 60 days, 120 days and 180 days of natural aging, respectively. Then accelerated test is carried out to predict the long-term performance of FFRP. The results show that short-term exposure test (just considering the temperature and humidity) cannot achieve the same effect on mechanical property degradation as natural aging. A modified residual mechanical property model of FFRP is established according to the test results.

Název v anglickém jazyce

Degradation of bending properties of flax fiber reinforced polymer after natural aging and accelerated aging

Popis výsledku anglicky

In this paper, the effect of natural aging and accelerated aging on the bending properties of flax fiber reinforced polymer (FFRP) is studied. Test results show that the flexural strength decreases by 11.2%, 14.9%, 15.5%, and the flexural modulus decreases by 21.3%, 32.3%, 35.8%, after 60 days, 120 days and 180 days of natural aging, respectively. Then accelerated test is carried out to predict the long-term performance of FFRP. The results show that short-term exposure test (just considering the temperature and humidity) cannot achieve the same effect on mechanical property degradation as natural aging. A modified residual mechanical property model of FFRP is established according to the test results.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20102 - Construction engineering, Municipal and structural engineering

Projekt

<a href="/cs/project/EF16_025%2F0007293" target="_blank" >EF16_025/0007293: Modulární platforma pro autonomní podvozky specializovaných elektrovozidel pro dopravu nákladu a zařízení</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Construction and Building Materials

ISSN

0950-0618

e-ISSN

—

Svazek periodika

240

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000527362400028

EID výsledku v databázi Scopus

2-s2.0-85077495475