Mechanical, morphological, and dimensional properties of heat-treated fused deposition modeling printed polymeric matrix of polyethylene terephthalate glycol

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24620%2F24%3A00013021" target="_blank" >RIV/46747885:24620/24:00013021 - isvavai.cz</a>

Výsledek na webu

<a href="https://journals.sagepub.com/doi/epdf/10.1177/14777606231218354?src=getftr&utm_source=scopus&getft_integrator=scopus" target="_blank" >https://journals.sagepub.com/doi/epdf/10.1177/14777606231218354?src=getftr&utm_source=scopus&getft_integrator=scopus</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1177/14777606231218354" target="_blank" >10.1177/14777606231218354</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical, morphological, and dimensional properties of heat-treated fused deposition modeling printed polymeric matrix of polyethylene terephthalate glycol

Popis výsledku v původním jazyce

This study investigates the impact of heat treatment on the mechanical, morphological, and dimensional properties of polyethylene terephthalate glycol (PETG), a commonly used thermoplastic in 3D printing. Taguchi L25 orthogonal array (OA) was employed to optimize 3D printing parameters, considering factors such as infill percentage (ranging from 20% to 100%), layer height (0.12 mm to 0.28 mm), layer width (0.32 mm to 0.62 mm), and infill pattern. Following ASTM D638 type IV standards, mechanical testing revealed that the optimal printing conditions included a 100% infill percentage, a layer height of 0.16 mm, a layer width of 0.32 mm, and an infill pattern of 5. Specimen 22, produced under these conditions, exhibited a notable stress-bearing capacity of 46.43 ± 1.394 MPa. These results are consistent with previous studies that underscored the significance of high infill percentages and finer layer dimensions in enhancing tensile properties. Subsequently, these optimized specimens were exposed to various heat treatment conditions. It was discovered that heat treatment at 85°C for 15 min yielded the most significant improvements, increasing the stress-bearing capacity to 53.462 ± 1.604 MPa, representing an impressive ∼16% enhancement compared to non-heat-treated specimens. However, this treatment also led to increased brittleness. Morphological analysis using Scanning Electron Microscopy (SEM) further substantiated the findings. Specimens subjected to heat treatment at 85°C exhibited fewer voids and porosities than those printed with lower infill percentages and larger layer dimensions. These observations underscored the importance of adequate infill density and finer printing details for optimizing strength. Regarding dimensional stability, dimensional changes were meticulously measured after heat treatment. Notably, specimens subjected to heat treatment at or near the glass transition temperature (Tg) of PETG experienced the most significant shrinkage. Specimen 6, treated at 85°C, displayed the highest shrinkage, with length and width reductions of 133.30 ± 3.85 mm and 25.90 ± 0.87 mm, respectively.

Název v anglickém jazyce

Mechanical, morphological, and dimensional properties of heat-treated fused deposition modeling printed polymeric matrix of polyethylene terephthalate glycol

Popis výsledku anglicky

This study investigates the impact of heat treatment on the mechanical, morphological, and dimensional properties of polyethylene terephthalate glycol (PETG), a commonly used thermoplastic in 3D printing. Taguchi L25 orthogonal array (OA) was employed to optimize 3D printing parameters, considering factors such as infill percentage (ranging from 20% to 100%), layer height (0.12 mm to 0.28 mm), layer width (0.32 mm to 0.62 mm), and infill pattern. Following ASTM D638 type IV standards, mechanical testing revealed that the optimal printing conditions included a 100% infill percentage, a layer height of 0.16 mm, a layer width of 0.32 mm, and an infill pattern of 5. Specimen 22, produced under these conditions, exhibited a notable stress-bearing capacity of 46.43 ± 1.394 MPa. These results are consistent with previous studies that underscored the significance of high infill percentages and finer layer dimensions in enhancing tensile properties. Subsequently, these optimized specimens were exposed to various heat treatment conditions. It was discovered that heat treatment at 85°C for 15 min yielded the most significant improvements, increasing the stress-bearing capacity to 53.462 ± 1.604 MPa, representing an impressive ∼16% enhancement compared to non-heat-treated specimens. However, this treatment also led to increased brittleness. Morphological analysis using Scanning Electron Microscopy (SEM) further substantiated the findings. Specimens subjected to heat treatment at 85°C exhibited fewer voids and porosities than those printed with lower infill percentages and larger layer dimensions. These observations underscored the importance of adequate infill density and finer printing details for optimizing strength. Regarding dimensional stability, dimensional changes were meticulously measured after heat treatment. Notably, specimens subjected to heat treatment at or near the glass transition temperature (Tg) of PETG experienced the most significant shrinkage. Specimen 6, treated at 85°C, displayed the highest shrinkage, with length and width reductions of 133.30 ± 3.85 mm and 25.90 ± 0.87 mm, respectively.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2024

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Progress in Rubber Plastics and Recycling Technology

ISSN

1477-7606

e-ISSN

—

Svazek periodika

40

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

23

Strana od-do

168-190

Kód UT WoS článku

001107785800001

EID výsledku v databázi Scopus

2-s2.0-85177669665