The influence of thermally sprayed coatings microstructure on their mechanical and tribological characteristics
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F08%3A%230000348" target="_blank" >RIV/47718684:_____/08:#0000348 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The influence of thermally sprayed coatings microstructure on their mechanical and tribological characteristics
Popis výsledku v původním jazyce
The paper is focused on studying the coatings microstructure and mechanical properties. Four different tests of wear resistance were done to study the mechanism of surface degradation, to confirm the results of mechanical testing and to predict the lifetime of coated parts - the abrasive wear performance of the coatings was assessed using a dry/sand rubber wheel test according to ASTM G-65, wet slurry abrasion test according to ASTM G-75, pin-on-disc test according to ASTM G-99 and erosion wear resistance for three impact angles. On the basis of obtained data the new possibilities of coatings application was determined, tested and implemented.
Název v anglickém jazyce
The influence of thermally sprayed coatings microstructure on their mechanical and tribological characteristics
Popis výsledku anglicky
The paper is focused on studying the coatings microstructure and mechanical properties. Four different tests of wear resistance were done to study the mechanism of surface degradation, to confirm the results of mechanical testing and to predict the lifetime of coated parts - the abrasive wear performance of the coatings was assessed using a dry/sand rubber wheel test according to ASTM G-65, wet slurry abrasion test according to ASTM G-75, pin-on-disc test according to ASTM G-99 and erosion wear resistance for three impact angles. On the basis of obtained data the new possibilities of coatings application was determined, tested and implemented.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/OC%20532.002" target="_blank" >OC 532.002: Vliv mikrostruktury žárově stříkaných povlaků na jejich tribologické charakteristiky</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science Forum
ISSN
0255-5476
e-ISSN
—
Svazek periodika
2008
Číslo periodika v rámci svazku
567-568
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000253516900052
EID výsledku v databázi Scopus
—