Weld joints of wrought and cast creep resistant steel P91 ? mechanical properties and structural stability

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F09%3A%230000361" target="_blank" >RIV/47718684:_____/09:#0000361 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Weld joints of wrought and cast creep resistant steel P91 ? mechanical properties and structural stability

Popis výsledku v původním jazyce

Two trial weld joints of creep resistant 9Cr-1Mo-V steel used for production of steam pipes and cast components of steam power plants were undergone long-term creep testing at a temperature range from 525 °C to 625 °C.Up to 575 °C the creep resistance ofthe both weld joints ranges in recommended 20% scatter band of the creep rupture strength of the base material; at 600 °C and 625 °C it falls below the bottom of this scatter band. A critical region is a fine grain heat affected zone of the base material. Causes of the preferential creep failure in this region are a relatively high density of coarse particles of secondary phases at grain and subgrain boundaries and a low density of fine intragranular precipitate, which is gradually resolved and is replaced with Z-phase particles.

Název v anglickém jazyce

Weld joints of wrought and cast creep resistant steel P91 ? mechanical properties and structural stability

Popis výsledku anglicky

Two trial weld joints of creep resistant 9Cr-1Mo-V steel used for production of steam pipes and cast components of steam power plants were undergone long-term creep testing at a temperature range from 525 °C to 625 °C.Up to 575 °C the creep resistance ofthe both weld joints ranges in recommended 20% scatter band of the creep rupture strength of the base material; at 600 °C and 625 °C it falls below the bottom of this scatter band. A critical region is a fine grain heat affected zone of the base material. Causes of the preferential creep failure in this region are a relatively high density of coarse particles of secondary phases at grain and subgrain boundaries and a low density of fine intragranular precipitate, which is gradually resolved and is replaced with Z-phase particles.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/OC09041" target="_blank" >OC09041: Mikrostrukturní výzkum svarových spojů progresivních žáropevných materiálů pro tepelné elektrárny</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

18th International Conference on Metallurgy and Materials

ISBN

978-80-87294-10-9

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Tanger Ltd.

Místo vydání

Ostrava

Místo konání akce

Hradec nad Moravicí

Datum konání akce

1. 1. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—