Microstructure Development during Creep Testing of P92 Steel Weld Joint

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F10%3A%230000425" target="_blank" >RIV/47718684:_____/10:#0000425 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructure Development during Creep Testing of P92 Steel Weld Joint

Popis výsledku v původním jazyce

One-side trial weld joint of W type was prepared from P92 type steel using GTAW & SMAW method in conditions used in idustrial praxis for production and repairing of parts of power plants. Creep test to the rupture of smooth cross-weld samples has been carried out. Fractographic analysis, hardness measurement and detailed study of submicrostructure have been performed . Changes of microstructure were correlated with the creep strength. Critical zone from a point of view of the creep failure is located inthe fine prior austenite grain heat affected zone and in the overheated zone of the base material.

Název v anglickém jazyce

Microstructure Development during Creep Testing of P92 Steel Weld Joint

Popis výsledku anglicky

One-side trial weld joint of W type was prepared from P92 type steel using GTAW & SMAW method in conditions used in idustrial praxis for production and repairing of parts of power plants. Creep test to the rupture of smooth cross-weld samples has been carried out. Fractographic analysis, hardness measurement and detailed study of submicrostructure have been performed . Changes of microstructure were correlated with the creep strength. Critical zone from a point of view of the creep failure is located inthe fine prior austenite grain heat affected zone and in the overheated zone of the base material.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca Conference

ISSN

1338-1660

e-ISSN

—

Svazek periodika

2010

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—