Structure and mechanical properties of cast steel microalloyed with titanium and vanadiumt
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F10%3A%230000426" target="_blank" >RIV/47718684:_____/10:#0000426 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Structure and mechanical properties of cast steel microalloyed with titanium and vanadiumt
Popis výsledku v původním jazyce
Three trial melts of manganese steel (reference steel, steel microalloyed with titanium and steel microalloyed with titanium and vanadium) underwent special heat treatment. The goal of thework was an improvement of mechanical properties using effect of microalloyed elements and heat treatment. A mixtured structure of bainite, acicular and polygonal ferrite was obtained after the optimum heat treatment of microalloyed steels. The yield stress and ultimate tensile strength increased from 410 MPa and 566 MPa of the reference steel to 817 MPa and 909 MPa of the steel with titanium and vanadium additions respectively. At the same time notch toughness decreased from 180 J/cm2 to 63 J/cm2.
Název v anglickém jazyce
Structure and mechanical properties of cast steel microalloyed with titanium and vanadiumt
Popis výsledku anglicky
Three trial melts of manganese steel (reference steel, steel microalloyed with titanium and steel microalloyed with titanium and vanadium) underwent special heat treatment. The goal of thework was an improvement of mechanical properties using effect of microalloyed elements and heat treatment. A mixtured structure of bainite, acicular and polygonal ferrite was obtained after the optimum heat treatment of microalloyed steels. The yield stress and ultimate tensile strength increased from 410 MPa and 566 MPa of the reference steel to 817 MPa and 909 MPa of the steel with titanium and vanadium additions respectively. At the same time notch toughness decreased from 180 J/cm2 to 63 J/cm2.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Metallurgica Slovaca Conference
ISSN
1338-1660
e-ISSN
—
Svazek periodika
2010
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
6
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—