Assessment of remaining lifetime of the boiler tube and microstructure analysis

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F13%3A%230000554" target="_blank" >RIV/47718684:_____/13:#0000554 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.vtt.fi/publications/index.jsp" target="_blank" >http://www.vtt.fi/publications/index.jsp</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Assessment of remaining lifetime of the boiler tube and microstructure analysis

Popis výsledku v původním jazyce

Assessment of remaining lifetime represents a very complicated problem, which needs the knowledge of degradation processes in the material of a component, and also the service conditions of the components, e.g. way of loading and the influence of the surrounding environment. There is a common interest to operate the produced components as effectively as possible and thus as long as possible without reducing their safety and reliability, what could cause economic and human losses. This is a problem of safe operation and its prolongation in justifiable cases. As a result of new modern and more resistant materials development, the general interest is to be able to evaluate the extent and rate of degradation processes at various service conditions, mainlyto prevent the components from brittle fracture. The goal even in the stage of a component design is to guarantee their longtime operation. At present, the assessment of component material microstructure is one of the methods that makes i

Název v anglickém jazyce

Assessment of remaining lifetime of the boiler tube and microstructure analysis

Popis výsledku anglicky

Assessment of remaining lifetime represents a very complicated problem, which needs the knowledge of degradation processes in the material of a component, and also the service conditions of the components, e.g. way of loading and the influence of the surrounding environment. There is a common interest to operate the produced components as effectively as possible and thus as long as possible without reducing their safety and reliability, what could cause economic and human losses. This is a problem of safe operation and its prolongation in justifiable cases. As a result of new modern and more resistant materials development, the general interest is to be able to evaluate the extent and rate of degradation processes at various service conditions, mainlyto prevent the components from brittle fracture. The goal even in the stage of a component design is to guarantee their longtime operation. At present, the assessment of component material microstructure is one of the methods that makes i

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/TE01020068" target="_blank" >TE01020068: Centrum výzkumu a experimentálního vývoje spolehlivé energetiky</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of International Conference on Life Management and Maintenance for Power Plants Baltica IX, Edited by Pertti Auerkari & Juha Veivo

ISBN

978-951-38-8025-5

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

477-493

Název nakladatele

VTT TECHNOLOGY 106

Místo vydání

Helsinky

Místo konání akce

Helsinky

Datum konání akce

1. 1. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—