CORROSION BEHAVIOR OF SELECTED HVOF THERMALLY SPRAYED COATINGS IN AGGRESSIVE ENVIRONMENTS
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F14%3A%230000555" target="_blank" >RIV/47718684:_____/14:#0000555 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
CORROSION BEHAVIOR OF SELECTED HVOF THERMALLY SPRAYED COATINGS IN AGGRESSIVE ENVIRONMENTS
Popis výsledku v původním jazyce
Corrosion resistant coatings must exhibit high density (low porosity), good adhesion to the substrate and of course low penetration of oxides. This paper deals with corrosion resistance comparison of six corrosion resistant coatings, which are frequentlyused in power plants. The comparison of following coatings is described: two cermet coatings Cr3C2-NiCr and Cr3C2-CoNiCrAlY, one experimental coating TiMoCN-Ni, and three alloy based coatings CoCrWC (Stellite 6), Hastelloy C-276 and NiCrBSi. Each of these six coatings was evaluated using immersion corrosion tests in two selected corrosive aggressive environments. Aqueous solution of 5% H2(SO)4 and artificial seawater were selected as corrosive aggressive environments. All coatings were deposited on W.Nr. 1.0553 carbon steel using thermal spraying technology HP/HVOF (High Pressure/High Velocity Oxygen Fuel). Carbon steel was used as the base material mainly to determine if the open porosity of evaluated coatings does not pose a problem
Název v anglickém jazyce
CORROSION BEHAVIOR OF SELECTED HVOF THERMALLY SPRAYED COATINGS IN AGGRESSIVE ENVIRONMENTS
Popis výsledku anglicky
Corrosion resistant coatings must exhibit high density (low porosity), good adhesion to the substrate and of course low penetration of oxides. This paper deals with corrosion resistance comparison of six corrosion resistant coatings, which are frequentlyused in power plants. The comparison of following coatings is described: two cermet coatings Cr3C2-NiCr and Cr3C2-CoNiCrAlY, one experimental coating TiMoCN-Ni, and three alloy based coatings CoCrWC (Stellite 6), Hastelloy C-276 and NiCrBSi. Each of these six coatings was evaluated using immersion corrosion tests in two selected corrosive aggressive environments. Aqueous solution of 5% H2(SO)4 and artificial seawater were selected as corrosive aggressive environments. All coatings were deposited on W.Nr. 1.0553 carbon steel using thermal spraying technology HP/HVOF (High Pressure/High Velocity Oxygen Fuel). Carbon steel was used as the base material mainly to determine if the open porosity of evaluated coatings does not pose a problem
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/TA02010486" target="_blank" >TA02010486: Výzkum a vývoj žárově stříkaných povlaků pro energetický průmysl</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2014 23th International Conference on Metallurgy and Materials
ISBN
978-80-87294-54-3
ISSN
—
e-ISSN
—
Počet stran výsledku
1981
Strana od-do
940-946
Název nakladatele
TANGER Ltd.
Místo vydání
Ostrava, Czech Republic, EU
Místo konání akce
Hotel Voronez I, Brno, Czech Republic, EU
Datum konání akce
1. 1. 2014
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—