Srovnání intezity vysokoteplotního povrchového poškození oceli 20MoCrS4 při různých parametrech dynamického ohřevu

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F06%3A00000023" target="_blank" >RIV/49777513:23210/06:00000023 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Comparison of intensity of high temperature surface damage for 20MoCrS4 steel with varying parameters of dynamical heating

Popis výsledku v původním jazyce

During heating to the forming temperature in hot or warm forming operations, semiproducts are exposed to high temperatures in direct contact with corrosion environment for a certain period of time. Using protective atmospheres in mass production is unsuitable for economical reasons. To minimise the influence of heating on the surface degradation, it is necessary to reach the desired temperature and uniform temperature field as quickly as possible, yet in compliance with physical properties of the heatedmaterial and with the technology in use. The experiments were focused on investigation of various temperatures and heating times simulating conditions of dynamical and classical processes. The comparison of the influence of heating temperature and timeon the iron scale occurrence intensity as well as the influence on the surface layers of the semiproducts was performed.

Název v anglickém jazyce

Comparison of intensity of high temperature surface damage for 20MoCrS4 steel with varying parameters of dynamical heating

Popis výsledku anglicky

During heating to the forming temperature in hot or warm forming operations, semiproducts are exposed to high temperatures in direct contact with corrosion environment for a certain period of time. Using protective atmospheres in mass production is unsuitable for economical reasons. To minimise the influence of heating on the surface degradation, it is necessary to reach the desired temperature and uniform temperature field as quickly as possible, yet in compliance with physical properties of the heatedmaterial and with the technology in use. The experiments were focused on investigation of various temperatures and heating times simulating conditions of dynamical and classical processes. The comparison of the influence of heating temperature and timeon the iron scale occurrence intensity as well as the influence on the surface layers of the semiproducts was performed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JP - Průmyslové procesy a zpracování

OECD FORD obor

—

Projekt

<a href="/cs/project/1M06032" target="_blank" >1M06032: VÝZKUMNÉ CENTRUM TVÁŘECÍCH TECHNOLOGIÍ</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materiáls Science and Technology

ISSN

0267-0836

e-ISSN

—

Svazek periodika

—

Číslo periodika v rámci svazku

—

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

5

Strana od-do

1444

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—