Optimization of Q-P Process Parameters with Regard to Final Microstructures and Properties

Popis výsledku v původním jazyce

This paper presents optimization of heat treatment conditions of low-alloyed 42SiCr steel. This steel possesses in basic state the strength of 980 MPa and ductility of 30%. Through the conventional treatment very high strength can be reached, but the ductility drops down to lower values. Due to the heat treatment designed according to Q-P (Quenching & Partitioning) method, the strength of this steel can be improved up to 2000 MPa while keeping the ductility over 10%. The parameters of Q-P process have been optimized with respect to final microstructures and properties. The influence of various parameters on the structure development was documented by light and confocal microscopy and the resulting mechanical properties were measured. Key words: high strength steel, Q-P process.

Název v anglickém jazyce

Optimization of Q-P Process Parameters with Regard to Final Microstructures and Properties

Popis výsledku anglicky

This paper presents optimization of heat treatment conditions of low-alloyed 42SiCr steel. This steel possesses in basic state the strength of 980 MPa and ductility of 30%. Through the conventional treatment very high strength can be reached, but the ductility drops down to lower values. Due to the heat treatment designed according to Q-P (Quenching & Partitioning) method, the strength of this steel can be improved up to 2000 MPa while keeping the ductility over 10%. The parameters of Q-P process have been optimized with respect to final microstructures and properties. The influence of various parameters on the structure development was documented by light and confocal microscopy and the resulting mechanical properties were measured. Key words: high strength steel, Q-P process.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/1M06032" target="_blank" >1M06032: VÝZKUMNÉ CENTRUM TVÁŘECÍCH TECHNOLOGIÍ</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Annals of DAAAM for 2009 & Proceedings of the 20th international DAAAM symposium

ISBN

—

ISSN

1726-9679

e-ISSN

—

Počet stran výsledku

2

Strana od-do

—

Název nakladatele

DAAAM International

Místo vydání

Vienna

Místo konání akce

Vienna, Austria

Datum konání akce

28. 11. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—