Miniaturization in Thixoforming

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F10%3A00503749" target="_blank" >RIV/49777513:23210/10:00503749 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Miniaturization in Thixoforming

Popis výsledku v původním jazyce

Innovative technological processes can help us to obtain unconventional structures with specific mechanical properties, even from conventional materials. Forming metal alloys in the semi-solid state is one of many ways. With thixoforming the tool steel X210Cr12 was treated with rapid solidification from the liquid phase. The microstructure after processing in the semi-solid state is 96% globular austenite formations surrounded by a carbide network. The aim of the experiment was to test the new technological process and to describe the obtained microstructure and its stability. The stability of the microstructure was tested under various thermal constraints and mechanical loading. The hardness of the austenite component after thixoforming was about 320HV 0.05; hardness of the carbide network was about 550 HV 0.05.

Název v anglickém jazyce

Miniaturization in Thixoforming

Popis výsledku anglicky

Innovative technological processes can help us to obtain unconventional structures with specific mechanical properties, even from conventional materials. Forming metal alloys in the semi-solid state is one of many ways. With thixoforming the tool steel X210Cr12 was treated with rapid solidification from the liquid phase. The microstructure after processing in the semi-solid state is 96% globular austenite formations surrounded by a carbide network. The aim of the experiment was to test the new technological process and to describe the obtained microstructure and its stability. The stability of the microstructure was tested under various thermal constraints and mechanical loading. The hardness of the austenite component after thixoforming was about 320HV 0.05; hardness of the carbide network was about 550 HV 0.05.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JQ - Strojní zařízení a nástroje

OECD FORD obor

—

Projekt

<a href="/cs/project/1M06032" target="_blank" >1M06032: VÝZKUMNÉ CENTRUM TVÁŘECÍCH TECHNOLOGIÍ</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

MM Science Journal

ISSN

1803-1269

e-ISSN

—

Svazek periodika

4

Číslo periodika v rámci svazku

December

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

3

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—