Influence of the Surface Quality on the Stress State During Rotary Bending Test

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F11%3A43897080" target="_blank" >RIV/49777513:23210/11:43897080 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of the Surface Quality on the Stress State During Rotary Bending Test

Popis výsledku v původním jazyce

The state of the surface layer and the used manufacturing process strongly influence the life of single components. By the fatigue loading, a small surface roughness and residual stresses put into the material during the whole production process can rapidly affect the final stress state. Determination of final stresses is quite difficult technical problem in practical conditions. An alternative possibility represents the application of the FEM simulation. In the paper, simulation models of the test specimen during the rotation bending test are presented. The stress fields in the specimen with real surface roughness and with integrated values of residual stresses experimentally measured using the X-ray diffraction are compared with the stress field in aspecimen with ideally smooth surface.

Název v anglickém jazyce

Influence of the Surface Quality on the Stress State During Rotary Bending Test

Popis výsledku anglicky

The state of the surface layer and the used manufacturing process strongly influence the life of single components. By the fatigue loading, a small surface roughness and residual stresses put into the material during the whole production process can rapidly affect the final stress state. Determination of final stresses is quite difficult technical problem in practical conditions. An alternative possibility represents the application of the FEM simulation. In the paper, simulation models of the test specimen during the rotation bending test are presented. The stress fields in the specimen with real surface roughness and with integrated values of residual stresses experimentally measured using the X-ray diffraction are compared with the stress field in aspecimen with ideally smooth surface.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/1M06032" target="_blank" >1M06032: VÝZKUMNÉ CENTRUM TVÁŘECÍCH TECHNOLOGIÍ</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Annals of DAAAM for 2011 & Proceedings of the 22nd international DAAAM symposium

ISBN

978-3-901509-83-4

ISSN

1726-9679

e-ISSN

—

Počet stran výsledku

2

Strana od-do

0123-0124

Název nakladatele

DAAAM International Vienna 2011

Místo vydání

Vienna

Místo konání akce

Vienna, Austrálie

Datum konání akce

23. 11. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—