Low-cost and Time-saving Thermomechanical Treatment on the 54SiCr Steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F13%3A43920762" target="_blank" >RIV/49777513:23210/13:43920762 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1002/9781118792148.ch85" target="_blank" >http://dx.doi.org/10.1002/9781118792148.ch85</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1002/9781118792148.ch85" target="_blank" >10.1002/9781118792148.ch85</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Low-cost and Time-saving Thermomechanical Treatment on the 54SiCr Steel
Popis výsledku v původním jazyce
Decrease of energy costs for annealing to improve the formability of cold forming steel is a hot topic nowadays. The processing time during common soft annealing is approximately in hours. Low-temperature, energy efficient thermomechanical treatment wasdeveloped for significant time reduction to a few tens of seconds. It enables a change of morphology from lamellar into the spheroidised form together with refinement of ferritic grains. 54SiCr steel with initial lamellar ferritic-pearlitic structure wasused for the experiment. During experimental processing optimization the A c1 temperature was determined for different heating rates. Next, the appropriate heating and deformation temperature was determined as well. The main part of the research was todescribe the influence of deformation intensity and holding time between deformations for carbide spheroidisation and recrystallization of ferritic grains. The recrystallized structure which contained ferrite with dispersed spheroidised c
Název v anglickém jazyce
Low-cost and Time-saving Thermomechanical Treatment on the 54SiCr Steel
Popis výsledku anglicky
Decrease of energy costs for annealing to improve the formability of cold forming steel is a hot topic nowadays. The processing time during common soft annealing is approximately in hours. Low-temperature, energy efficient thermomechanical treatment wasdeveloped for significant time reduction to a few tens of seconds. It enables a change of morphology from lamellar into the spheroidised form together with refinement of ferritic grains. 54SiCr steel with initial lamellar ferritic-pearlitic structure wasused for the experiment. During experimental processing optimization the A c1 temperature was determined for different heating rates. Next, the appropriate heating and deformation temperature was determined as well. The main part of the research was todescribe the influence of deformation intensity and holding time between deformations for carbide spheroidisation and recrystallization of ferritic grains. The recrystallized structure which contained ferrite with dispersed spheroidised c
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
PRICM 8
ISBN
978-0-470-94309-0
ISSN
—
e-ISSN
—
Počet stran výsledku
7
Strana od-do
679-685
Název nakladatele
Wiley
Místo vydání
Hoboken
Místo konání akce
Waikoloa, Hawaii, USA
Datum konání akce
4. 8. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—