Optimisation of the Q-P Process Parameters for Low Alloyed Steels with 0.2% C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F14%3A43923910" target="_blank" >RIV/49777513:23210/14:43923910 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.2478/amm-2014-0209" target="_blank" >http://dx.doi.org/10.2478/amm-2014-0209</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.2478/amm-2014-0209" target="_blank" >10.2478/amm-2014-0209</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Optimisation of the Q-P Process Parameters for Low Alloyed Steels with 0.2% C

Popis výsledku v původním jazyce

In steels which are treated by the quenching and partitioning (Q&P) process, carbon content is one of the crucial parameters because carbon contributes greatly to stabilization of retained austenite and strengthens the material. In the present study, theQ&P process was gradually optimised for two low-alloyed steels with 0.2 % carbon content and with and without Cr addition. The results show that the cooling rate, as well as the austenitizing temperature, has a pronounced effect on microstructure evolution. The strength and elongation in the Mn, Si and Cr-alloyed steel was approx. 900 MPa and more than 30 %, respectively.

Název v anglickém jazyce

Optimisation of the Q-P Process Parameters for Low Alloyed Steels with 0.2% C

Popis výsledku anglicky

In steels which are treated by the quenching and partitioning (Q&P) process, carbon content is one of the crucial parameters because carbon contributes greatly to stabilization of retained austenite and strengthens the material. In the present study, theQ&P process was gradually optimised for two low-alloyed steels with 0.2 % carbon content and with and without Cr addition. The results show that the cooling rate, as well as the austenitizing temperature, has a pronounced effect on microstructure evolution. The strength and elongation in the Mn, Si and Cr-alloyed steel was approx. 900 MPa and more than 30 %, respectively.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GPP107%2F12%2FP960" target="_blank" >GPP107/12/P960: Ovlivňování mechanických vlastností AHS oceli modifikací struktury</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Archives of Metallurgy and Materials

ISSN

1733-3490

e-ISSN

—

Svazek periodika

59

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

6

Strana od-do

1205-1210

Kód UT WoS článku

000345100000066

EID výsledku v databázi Scopus

—