The Effect of Alloying on Mechanical Properties of Advanced High Strength Steels
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F14%3A43923966" target="_blank" >RIV/49777513:23210/14:43923966 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.2478/amm-2014-0206" target="_blank" >http://dx.doi.org/10.2478/amm-2014-0206</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.2478/amm-2014-0206" target="_blank" >10.2478/amm-2014-0206</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The Effect of Alloying on Mechanical Properties of Advanced High Strength Steels
Popis výsledku v původním jazyce
uenching and partitioning process with incorporated incremental deformation was optimized for six high strength steels with various contents of carbon (0.4-0.6%), manganese (0.6-1.2), silicon (2-2.6%) and chromium (0.8-1.3%). The optimization was gradually done for each steel with respect to the final microstructures and properties. The effect of cooling rate, quenching and partitioning temperature on microstructure development was further investigated. Interesting combinations of mechanical propertieswere obtained, with tensile strength in the region of 1600-2400 MPa and ductility of 6-20%. Przeprowadzono optymalizacje procesu hartowania i partycjonowania węgla (Quenching and Partitioning - Q&P) w połączeniu ze stopniowymi przyrostami odkształcenia dla sześciu wysokowytrzymałych stali o różnej zawartości węgla (0, 4-0, 6%) manganu (0, 6-1, 2%), krzemu (2-2, 6%) oraz chromu (0, 8-1, 3%). Optymalizacje prowadzono dla kazdej stali stopniowo pod katem końcowej mikrostruktury i właściwośc
Název v anglickém jazyce
The Effect of Alloying on Mechanical Properties of Advanced High Strength Steels
Popis výsledku anglicky
uenching and partitioning process with incorporated incremental deformation was optimized for six high strength steels with various contents of carbon (0.4-0.6%), manganese (0.6-1.2), silicon (2-2.6%) and chromium (0.8-1.3%). The optimization was gradually done for each steel with respect to the final microstructures and properties. The effect of cooling rate, quenching and partitioning temperature on microstructure development was further investigated. Interesting combinations of mechanical propertieswere obtained, with tensile strength in the region of 1600-2400 MPa and ductility of 6-20%. Przeprowadzono optymalizacje procesu hartowania i partycjonowania węgla (Quenching and Partitioning - Q&P) w połączeniu ze stopniowymi przyrostami odkształcenia dla sześciu wysokowytrzymałych stali o różnej zawartości węgla (0, 4-0, 6%) manganu (0, 6-1, 2%), krzemu (2-2, 6%) oraz chromu (0, 8-1, 3%). Optymalizacje prowadzono dla kazdej stali stopniowo pod katem końcowej mikrostruktury i właściwośc
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Archives of Metallurgy and Materials
ISSN
1733-3490
e-ISSN
—
Svazek periodika
3
Číslo periodika v rámci svazku
59
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
4
Strana od-do
1189-1192
Kód UT WoS článku
000345100000063
EID výsledku v databázi Scopus
—