Influence of Higher Stabilization Temperatures on the Microstructure and Mechanical Properties of Austenitic Stainless Steel 08Ch18N10T

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F23%3A43970824" target="_blank" >RIV/49777513:23210/23:43970824 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/49777513:23640/23:43970824

Výsledek na webu

<a href="https://www.mdpi.com/2075-4701/13/5/975" target="_blank" >https://www.mdpi.com/2075-4701/13/5/975</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/met13050975" target="_blank" >10.3390/met13050975</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Higher Stabilization Temperatures on the Microstructure and Mechanical Properties of Austenitic Stainless Steel 08Ch18N10T

Popis výsledku v původním jazyce

Precipitation strengthening in titanium-stabilized austenitic stainless steels can improve the hot yield strength, as requested, e.g., for nuclear industry applications. The resulting properties depend mainly on the parameters of the heat treatment and previous forming. The influence of the heat treatment parameters on the development of the microstructure and mechanical properties was determined for steel 08Ch18N10T (GOST). Solution annealing and stabilization with different temperatures and holds were performed on the steel, which was, in delivered condition, stabilized at 720 °C. Heat-treated samples were subjected to static tensile testing at room temperature and at 350 °C, microstructural analysis using light, scanning electron and transmission electron microscopy focused on precipitates, and HV10 hardness testing. The strengthening mechanism and its dependence on the stabilization parameters are described. The results of the experiment show the influence of the state of the input material on the final effect of heat treatment—repeated heat treatment achieved lower-strength characteristics than the initial state, while almost all modes showed above-limit values for the mechanical properties. Stabilization temperatures of 720 to 800 °C were found to be optimal in terms of the achieved hot yield strength. At higher temperatures, slightly lower strengths were achieved, but at significantly shorter dwell times.

Název v anglickém jazyce

Influence of Higher Stabilization Temperatures on the Microstructure and Mechanical Properties of Austenitic Stainless Steel 08Ch18N10T

Popis výsledku anglicky

Precipitation strengthening in titanium-stabilized austenitic stainless steels can improve the hot yield strength, as requested, e.g., for nuclear industry applications. The resulting properties depend mainly on the parameters of the heat treatment and previous forming. The influence of the heat treatment parameters on the development of the microstructure and mechanical properties was determined for steel 08Ch18N10T (GOST). Solution annealing and stabilization with different temperatures and holds were performed on the steel, which was, in delivered condition, stabilized at 720 °C. Heat-treated samples were subjected to static tensile testing at room temperature and at 350 °C, microstructural analysis using light, scanning electron and transmission electron microscopy focused on precipitates, and HV10 hardness testing. The strengthening mechanism and its dependence on the stabilization parameters are described. The results of the experiment show the influence of the state of the input material on the final effect of heat treatment—repeated heat treatment achieved lower-strength characteristics than the initial state, while almost all modes showed above-limit values for the mechanical properties. Stabilization temperatures of 720 to 800 °C were found to be optimal in terms of the achieved hot yield strength. At higher temperatures, slightly lower strengths were achieved, but at significantly shorter dwell times.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metals

ISSN

2075-4701

e-ISSN

2075-4701

Svazek periodika

13

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

15

Strana od-do

—

Kód UT WoS článku

000996716600001

EID výsledku v databázi Scopus

2-s2.0-85160847170