Hard and superhard Zr-Ni-N nanocomposite films

Popis výsledku v původním jazyce

This article reports on the relationship between the structure and mechanical properties of Zr-Ni-N nanocomposite films prepared by d.c.-reactive magnetron sputtering of a ZrNi (90/10 at.%) alloyed target in a mixture of Ar and N2 onto steel substrates using a planar round unbalanced magnetron with a diameter of 100 mm. The Zr-Ni-N nanocomposite films represent a new material of the type nc-MeN/metal composed of a hard nc-ZrN phase and a soft Ni phase, where nc- denotes the nanocrystalline phase of zirconium nitride. It was found that (i) there is a strong correlation between the structure of the film, the content of Ni in the nanocomposite and the film properties; (ii) Zr-Ni-N films can form superhard films with a high hardness up to 57 GPa; and (iii)Zr-Ni-N films with the same hardness (H>40 GPa) can exhibit different structures and strongly differ in the size of nc-ZrNx grains of which they are composed.

Název v anglickém jazyce

Hard and superhard Zr-Ni-N nanocomposite films

Popis výsledku anglicky

This article reports on the relationship between the structure and mechanical properties of Zr-Ni-N nanocomposite films prepared by d.c.-reactive magnetron sputtering of a ZrNi (90/10 at.%) alloyed target in a mixture of Ar and N2 onto steel substrates using a planar round unbalanced magnetron with a diameter of 100 mm. The Zr-Ni-N nanocomposite films represent a new material of the type nc-MeN/metal composed of a hard nc-ZrN phase and a soft Ni phase, where nc- denotes the nanocrystalline phase of zirconium nitride. It was found that (i) there is a strong correlation between the structure of the film, the content of Ni in the nanocomposite and the film properties; (ii) Zr-Ni-N films can form superhard films with a high hardness up to 57 GPa; and (iii)Zr-Ni-N films with the same hardness (H>40 GPa) can exhibit different structures and strongly differ in the size of nc-ZrNx grains of which they are composed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Surface and Coatings Technology

ISSN

02578972

e-ISSN

—

Svazek periodika

Vol. 139

Číslo periodika v rámci svazku

leden

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

9

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—