Hodnocení indentační lomové houževnatostí žárově stříkaných povlaků

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F05%3A00500003" target="_blank" >RIV/49777513:23520/05:00500003 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/49777513:23210/05:00500003

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Evaluation of indentation fracture toughness of thermally sprayes coatings

Popis výsledku v původním jazyce

The presented paper is devoted to a determination of and experimental evaluation of the indentation fracture toughness of thermally sprayed coatings. Significant improvements have been made to increase the fracture toughness of ceramics, but brittlenesscontinues to keep ceramics from more widespread use. That is why our interest is focused on a study of mechanical properties of ceramics and cermets surface. For this purpose the Vickers hardness test was applied in a case when the material is surfficiently brittle and cracks occur in the corners of the indents. For better evaluatin of the intentation fracture toughness we have suggested experimental set for initiation of cracks extension due to the applied bending stresses.

Název v anglickém jazyce

Evaluation of indentation fracture toughness of thermally sprayes coatings

Popis výsledku anglicky

The presented paper is devoted to a determination of and experimental evaluation of the indentation fracture toughness of thermally sprayed coatings. Significant improvements have been made to increase the fracture toughness of ceramics, but brittlenesscontinues to keep ceramics from more widespread use. That is why our interest is focused on a study of mechanical properties of ceramics and cermets surface. For this purpose the Vickers hardness test was applied in a case when the material is surfficiently brittle and cracks occur in the corners of the indents. For better evaluatin of the intentation fracture toughness we have suggested experimental set for initiation of cracks extension due to the applied bending stresses.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/FF-P2%2F023" target="_blank" >FF-P2/023: Vývoj nových průmyslových aplikací HVOF stříkaných povlaků.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Vrstvy a povlaky 2005

ISBN

80-969310-1-6

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

DIGITAL GRAPHICS

Místo vydání

Trenčín

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—