The Off-axis behavior of unidirectional Fiber-reinforced plastic composite

Popis výsledku v původním jazyce

Numerical and experimental investigations of off-axis behavior of unidirectional Fiber-reinforced plastic composite consisting of carbon fibers and epoxy matrix are presented. Static tensile tests of thin carbon-epoxy composite strips with various fiberdirections were performed and simulated using finite element program. Puck?s action plane concept (failure criterion) and progressive failure analysis were used for damage prediction of tested thin strips. Non-linear stress-strain relation was used for modeling of the off-axis behavior. The relation between tensile force and displacement in the direction of loading force and ultimate tensile force which caused damage and ultimate displacement of specimens were measured and compared with the results of numerical simulation.

Název v anglickém jazyce

The Off-axis behavior of unidirectional Fiber-reinforced plastic composite

Popis výsledku anglicky

Numerical and experimental investigations of off-axis behavior of unidirectional Fiber-reinforced plastic composite consisting of carbon fibers and epoxy matrix are presented. Static tensile tests of thin carbon-epoxy composite strips with various fiberdirections were performed and simulated using finite element program. Puck?s action plane concept (failure criterion) and progressive failure analysis were used for damage prediction of tested thin strips. Non-linear stress-strain relation was used for modeling of the off-axis behavior. The relation between tensile force and displacement in the direction of loading force and ultimate tensile force which caused damage and ultimate displacement of specimens were measured and compared with the results of numerical simulation.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materiali in Tehnologije

ISSN

1580-2949

e-ISSN

—

Svazek periodika

42

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

SI - Slovinská republika

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—