Degradation of Mechanical Properties of Composite Caused by Cyclic Loading

Popis výsledku v původním jazyce

The paper deals with the fatigue of composite materials with a focus on reduction of mechanical properties of the composite under displacement controlled bending cyclic loading. The research is concerned about fatigue of carbon/epoxy composite material with three stacking sequences: [0]8, [90(2)/0(2)]s and [0(2)/90(2)]s. Displacement controlled bending cyclic loading experiments were performed to observe stiffness degradation. Rectangular specimens were used in bending tests in several stress amplitudes; stress ratio ranging from 0.02 to 0.06. During experiments the changes of composite stiffness were recorded. These records were evaluated by FEA. Residual strength was measured after cyclic loading.

Název v anglickém jazyce

Degradation of Mechanical Properties of Composite Caused by Cyclic Loading

Popis výsledku anglicky

The paper deals with the fatigue of composite materials with a focus on reduction of mechanical properties of the composite under displacement controlled bending cyclic loading. The research is concerned about fatigue of carbon/epoxy composite material with three stacking sequences: [0]8, [90(2)/0(2)]s and [0(2)/90(2)]s. Displacement controlled bending cyclic loading experiments were performed to observe stiffness degradation. Rectangular specimens were used in bending tests in several stress amplitudes; stress ratio ranging from 0.02 to 0.06. During experiments the changes of composite stiffness were recorded. These records were evaluated by FEA. Residual strength was measured after cyclic loading.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GD101%2F08%2FH068" target="_blank" >GD101/08/H068: Výzkum nových principů mechanických a biomechanických systémů s inteligentním chováním</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of 48th International Scientific Conference Experimental Stress Analysis 2010

ISBN

978-80-244-2533-7

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Palacky University

Místo vydání

Olomouc

Místo konání akce

Velké Losiny

Datum konání akce

31. 5. 2010

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—