Mechanical properties degradation of a glass fibre laminates under cyclic tension

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F11%3A43899233" target="_blank" >RIV/49777513:23520/11:43899233 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/49777513:23210/11:43899233

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical properties degradation of a glass fibre laminates under cyclic tension

Popis výsledku v původním jazyce

Composite materials are used in a wide range of applications such as automotive, aerospace or power generation industry. Most structural parts are dynamically loaded; thus, fatigue must be taken into consideration during the design process even in the case of composite laminates. The most promising way how to predict the fatigue deterioration and reduce necessary experimental input data at the same time seems to be the micro mechanics of failure. However, even this approach requires necessary experimental input data. This paper deals with the woven fabric E-glass epoxy matrix composite. Static and fatigue test were performed. The influence of aluminium shims attached to the specimen on static mechanical properties and fatigue life is shown. Residual tensile strength and residual longitudinal modulus of the woven fabric laminated composite specimens after cyclic loading were investigated.

Název v anglickém jazyce

Mechanical properties degradation of a glass fibre laminates under cyclic tension

Popis výsledku anglicky

Composite materials are used in a wide range of applications such as automotive, aerospace or power generation industry. Most structural parts are dynamically loaded; thus, fatigue must be taken into consideration during the design process even in the case of composite laminates. The most promising way how to predict the fatigue deterioration and reduce necessary experimental input data at the same time seems to be the micro mechanics of failure. However, even this approach requires necessary experimental input data. This paper deals with the woven fabric E-glass epoxy matrix composite. Static and fatigue test were performed. The influence of aluminium shims attached to the specimen on static mechanical properties and fatigue life is shown. Residual tensile strength and residual longitudinal modulus of the woven fabric laminated composite specimens after cyclic loading were investigated.

Druh

D - Stať ve sborníku

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings : 49th international scientific conference : Experimental stress analysis 2011

ISBN

978-80-214-4275-7

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

183-190

Název nakladatele

University of Technology

Místo vydání

Brno

Místo konání akce

Znojmo

Datum konání akce

6. 6. 2011

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—