Model of Progressive Failure of Composite Materials using 3D Puck Failure Criterion

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F16%3A43922879" target="_blank" >RIV/49777513:23520/16:43922879 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.17222/mit.2014.233" target="_blank" >http://dx.doi.org/10.17222/mit.2014.233</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.17222/mit.2014.233" target="_blank" >10.17222/mit.2014.233</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Model of Progressive Failure of Composite Materials using 3D Puck Failure Criterion

Popis výsledku v původním jazyce

The model of progressive failure of composite materials considering material non-linearity was developed and implemented into the Abaqus FE software. Extended Puck failure criterion for 3D stress state was used for failure prediction. Furthermore, a simplified approach for simulation of delamination was considered. For the progressive failure simulation, the stiffness matrix degradation was used and the degradation parameters were function of a fracture angle. The model was tested on problems of a pin-loaded composite plate and of a composite tube subjected to compressive loading perpendicular to the tube axis.

Název v anglickém jazyce

Model of Progressive Failure of Composite Materials using 3D Puck Failure Criterion

Popis výsledku anglicky

The model of progressive failure of composite materials considering material non-linearity was developed and implemented into the Abaqus FE software. Extended Puck failure criterion for 3D stress state was used for failure prediction. Furthermore, a simplified approach for simulation of delamination was considered. For the progressive failure simulation, the stiffness matrix degradation was used and the degradation parameters were function of a fracture angle. The model was tested on problems of a pin-loaded composite plate and of a composite tube subjected to compressive loading perpendicular to the tube axis.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materiali in Tehnologije

ISSN

1580-2949

e-ISSN

—

Svazek periodika

3

Číslo periodika v rámci svazku

50

Stát vydavatele periodika

SI - Slovinská republika

Počet stran výsledku

1

Strana od-do

319-322

Kód UT WoS článku

000385008500006

EID výsledku v databázi Scopus

2-s2.0-84975089709