Motorcycle Suits: Uniaxial and Biaxial Tensile Tests of Leather

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F17%3A43933038" target="_blank" >RIV/49777513:23520/17:43933038 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Motorcycle Suits: Uniaxial and Biaxial Tensile Tests of Leather

Popis výsledku v původním jazyce

This paper describes uniaxial and biaxial tests of leather samples. The tests were conducted on non-standardized samples. The uniaxial test was performed on 100 samples. The biaxial test was done on 20 samples. The aim of the uniaxial test was to obtain a reliable value of the leather ultimate strength, on a large population of samples. Additionally, this test revealed the differences in the ultimate strength between two relative perpendicular directions of cut. The biaxial test was used to obtain the stress-strain relationship and the ultimate strength. The stress-strain relationship will be used in the future to improve the constitutive material model of the leather. The biaxial test was conducted under four logarithmically graded clamps separation speeds (1, 10, 100, 1000 mm/min).

Název v anglickém jazyce

Motorcycle Suits: Uniaxial and Biaxial Tensile Tests of Leather

Popis výsledku anglicky

This paper describes uniaxial and biaxial tests of leather samples. The tests were conducted on non-standardized samples. The uniaxial test was performed on 100 samples. The biaxial test was done on 20 samples. The aim of the uniaxial test was to obtain a reliable value of the leather ultimate strength, on a large population of samples. Additionally, this test revealed the differences in the ultimate strength between two relative perpendicular directions of cut. The biaxial test was used to obtain the stress-strain relationship and the ultimate strength. The stress-strain relationship will be used in the future to improve the constitutive material model of the leather. The biaxial test was conducted under four logarithmically graded clamps separation speeds (1, 10, 100, 1000 mm/min).

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20301 - Mechanical engineering

Projekt

<a href="/cs/project/LO1506" target="_blank" >LO1506: Podpora udržitelnosti centra NTIS - Nové technologie pro informační společnost</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

EAN 2017 - 55th Conference on Experimental Stress Analysis 2017

ISBN

978-80-553-3167-6

ISSN

—

e-ISSN

neuvedeno

Počet stran výsledku

6

Strana od-do

435-440

Název nakladatele

Technical University of Košice

Místo vydání

Košice

Místo konání akce

Novy Smokovec; Slovakia

Datum konání akce

30. 5. 2017

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—