Comparative study of Thermally Sprayed Coatings Under Different types of Wear Conditions for Hard Chromium Replacement
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23640%2F11%3A43898573" target="_blank" >RIV/49777513:23640/11:43898573 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s11249-011-9791-9" target="_blank" >http://dx.doi.org/10.1007/s11249-011-9791-9</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s11249-011-9791-9" target="_blank" >10.1007/s11249-011-9791-9</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Comparative study of Thermally Sprayed Coatings Under Different types of Wear Conditions for Hard Chromium Replacement
Popis výsledku v původním jazyce
The tribological properties of the HVOF-sprayed coatings WC-17%Co, WC-10%Co4%Cr, WC-15% NiMoCrFeCo, Cr3C2-25%NiCr, (Ti,Mo)(C,N)-37%NiCo, NiCrSiB, AISI 316L and the plasma-sprayed Cr2O3 coating were compared with the properties of electrolytic hard chromeand surface-hardened steel. Four wear tests were done; the dry sand/rubber wheel test (ASTM G-65), the wet slurry abrasion test (ASTM G-75), the pin-on-disk test (ASTM G-99), and the erosion wear resistance, measured for three impact angles. In all tests, the HVOF-sprayed hardmetal coatings exhibited superior properties and can be recommended as a replacement for traditional surface treatments. Due to its brittleness, the plasma-sprayed Cr2O3 can only be recommended for pure abrasive wear. The tested HVOF-sprayed metallic coatings, NiCrSiB and AISI 316L, and should not be used under more demanding conditions. Based on the obtained data, the application possibilities and limitations of the reported coatings were determined.
Název v anglickém jazyce
Comparative study of Thermally Sprayed Coatings Under Different types of Wear Conditions for Hard Chromium Replacement
Popis výsledku anglicky
The tribological properties of the HVOF-sprayed coatings WC-17%Co, WC-10%Co4%Cr, WC-15% NiMoCrFeCo, Cr3C2-25%NiCr, (Ti,Mo)(C,N)-37%NiCo, NiCrSiB, AISI 316L and the plasma-sprayed Cr2O3 coating were compared with the properties of electrolytic hard chromeand surface-hardened steel. Four wear tests were done; the dry sand/rubber wheel test (ASTM G-65), the wet slurry abrasion test (ASTM G-75), the pin-on-disk test (ASTM G-99), and the erosion wear resistance, measured for three impact angles. In all tests, the HVOF-sprayed hardmetal coatings exhibited superior properties and can be recommended as a replacement for traditional surface treatments. Due to its brittleness, the plasma-sprayed Cr2O3 can only be recommended for pure abrasive wear. The tested HVOF-sprayed metallic coatings, NiCrSiB and AISI 316L, and should not be used under more demanding conditions. Based on the obtained data, the application possibilities and limitations of the reported coatings were determined.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FT-TA5%2F072" target="_blank" >FT-TA5/072: Výzkum a vývoj nových konstrukčních řešení pro zvyšování účinnosti a spolehlivosti energetických zařízení použitím technologie žárového nástřiku</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Tribology Letters
ISSN
1023-8883
e-ISSN
—
Svazek periodika
43
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
16
Strana od-do
139-154
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—