USE OF IRNDT EVALUATION FOR CRACK DETECTION INDUCED BY CYCLIC LOADING
Popis výsledku v původním jazyce
Infrared nondestructive testing is an inspection method based on an external excitation of a measured sample and a thermographic analysis of its thermal response. It often uses advanced evaluation techniques based on temperature spatial and temporal changes. IRNDT is a suitable method for an inspection of thin samples, near-surface layers and cracks. An application of IRNDT for detection of crack on mechanically cyclically loaded welded pipes is introduced in this contribution. The goal of the analysis was to detect location of the crack before this crack was created and visually detectable. Results showed that a thermographic record without an advanced IRNDT evaluation could detect crack just before the mechanically loaded pipe is starting to break down. An advanced IRNDT evaluation brought more evident indication of a position of the crack and its development during the test. The experiment, the evaluation method and the results are described and the IRNDT evaluation advantages and disadvantages are discussed in this contribution.
Název v anglickém jazyce
USE OF IRNDT EVALUATION FOR CRACK DETECTION INDUCED BY CYCLIC LOADING
Popis výsledku anglicky
Infrared nondestructive testing is an inspection method based on an external excitation of a measured sample and a thermographic analysis of its thermal response. It often uses advanced evaluation techniques based on temperature spatial and temporal changes. IRNDT is a suitable method for an inspection of thin samples, near-surface layers and cracks. An application of IRNDT for detection of crack on mechanically cyclically loaded welded pipes is introduced in this contribution. The goal of the analysis was to detect location of the crack before this crack was created and visually detectable. Results showed that a thermographic record without an advanced IRNDT evaluation could detect crack just before the mechanically loaded pipe is starting to break down. An advanced IRNDT evaluation brought more evident indication of a position of the crack and its development during the test. The experiment, the evaluation method and the results are described and the IRNDT evaluation advantages and disadvantages are discussed in this contribution.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Metal 2018
ISBN
978-80-87294-84-0
ISSN
—
e-ISSN
neuvedeno
Počet stran výsledku
6
Strana od-do
941-946
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
23. 5. 2018
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—