THE CHANGE OF NOTCH TOUGHNESS PARAMETERS OF STEEL AFTER APPLICATION OF PLASMA NITRIDING
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60162694%3AG43__%2F14%3A00515462" target="_blank" >RIV/60162694:G43__/14:00515462 - isvavai.cz</a>
Výsledek na webu
<a href="http://vavtest.unob.cz/registr" target="_blank" >http://vavtest.unob.cz/registr</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
THE CHANGE OF NOTCH TOUGHNESS PARAMETERS OF STEEL AFTER APPLICATION OF PLASMA NITRIDING
Popis výsledku v původním jazyce
The plasma nitriding is currently one of the most used technologies of the chemical-thermal treatment. This work deals the change of the notch toughness parameters of DIN 1654/4 steel (ČSN 41 2042.4) which was plasma nitrided under selected nitriding conditions: plasma sputtering (cleaning) at 480 (°C), nitriding at 500 (°C), process duration t = 10 and 20 (h), p = 280 (Pa), U = 530 (V) and variable gas mixture ratio of 24N2: 8H2 (l/h) and 8N2: 24H2 (l/h). The work confirmed that nitrided steel became more brittle but that for different gas composition, the notch toughness behaves quite distinctly. The toughness of steel increases with extension of time for gas ratio 24H2: 8N2 (l/h), but for gas ratio 8H2: 24N2 (l/h), the toughness decreases slightly with nitriding.duration.
Název v anglickém jazyce
THE CHANGE OF NOTCH TOUGHNESS PARAMETERS OF STEEL AFTER APPLICATION OF PLASMA NITRIDING
Popis výsledku anglicky
The plasma nitriding is currently one of the most used technologies of the chemical-thermal treatment. This work deals the change of the notch toughness parameters of DIN 1654/4 steel (ČSN 41 2042.4) which was plasma nitrided under selected nitriding conditions: plasma sputtering (cleaning) at 480 (°C), nitriding at 500 (°C), process duration t = 10 and 20 (h), p = 280 (Pa), U = 530 (V) and variable gas mixture ratio of 24N2: 8H2 (l/h) and 8N2: 24H2 (l/h). The work confirmed that nitrided steel became more brittle but that for different gas composition, the notch toughness behaves quite distinctly. The toughness of steel increases with extension of time for gas ratio 24H2: 8N2 (l/h), but for gas ratio 8H2: 24N2 (l/h), the toughness decreases slightly with nitriding.duration.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
KA - Vojenství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
ICMT´- 2014, International Conference on Military Technologies and Special Technologies 2014
ISBN
978-80-8075-639-0
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
66-73
Název nakladatele
Alexander Dubcek University of Trencin, Faculty of Special Technology
Místo vydání
Bratislava
Místo konání akce
Bratislava, Slovak Republic
Datum konání akce
14. 5. 2014
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—