The Assessment of Selected Mechanical Properties of Steel after Application of Plasma Nitriding
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60162694%3AG43__%2F15%3A00531372" target="_blank" >RIV/60162694:G43__/15:00531372 - isvavai.cz</a>
Výsledek na webu
<a href="http://vavtest.unob.cz/registr" target="_blank" >http://vavtest.unob.cz/registr</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The Assessment of Selected Mechanical Properties of Steel after Application of Plasma Nitriding
Popis výsledku v původním jazyce
The article deals with mechanical properties of plasma nitrided steel. Experimental work was focused on evalua-tion of influence of plasma nitriding process to notch toughness of steel, the experimental were realised on V-notch samples of size 10x10x55 mm (according to CSN ISO 148-1 standard). Nitrided layers were applied to steel 30CrMoV9 which were subsequently evaluated by metallographic, GDOES and microhardness method. The notch toughness tests of steel were carried out using the instrumental Charpyhammer at temperatures -40 °C, +21 °C and + 70 °C. The results of experiments showed that plasma nitriding process has a direct impact on change of notch toughness parameters. The notch toughness of plasma nitrided steel was significantly decreased. Themeasurements thereinafter showed that values of notch toughness at low temperature (-40 °C) decreased but also at higher temperature (+70 °C). It was found a dependence of notch toughness values of plasma nitrided steel between the testi
Název v anglickém jazyce
The Assessment of Selected Mechanical Properties of Steel after Application of Plasma Nitriding
Popis výsledku anglicky
The article deals with mechanical properties of plasma nitrided steel. Experimental work was focused on evalua-tion of influence of plasma nitriding process to notch toughness of steel, the experimental were realised on V-notch samples of size 10x10x55 mm (according to CSN ISO 148-1 standard). Nitrided layers were applied to steel 30CrMoV9 which were subsequently evaluated by metallographic, GDOES and microhardness method. The notch toughness tests of steel were carried out using the instrumental Charpyhammer at temperatures -40 °C, +21 °C and + 70 °C. The results of experiments showed that plasma nitriding process has a direct impact on change of notch toughness parameters. The notch toughness of plasma nitrided steel was significantly decreased. Themeasurements thereinafter showed that values of notch toughness at low temperature (-40 °C) decreased but also at higher temperature (+70 °C). It was found a dependence of notch toughness values of plasma nitrided steel between the testi
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
KA - Vojenství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Svazek periodika
15
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
9
Strana od-do
307-315
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—