Surface treatment technologies for wear resistance increasing of 42CrMo4 steel.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60162694%3AG43__%2F15%3A00531386" target="_blank" >RIV/60162694:G43__/15:00531386 - isvavai.cz</a>
Výsledek na webu
<a href="http://vavtest.unob.cz/registr" target="_blank" >http://vavtest.unob.cz/registr</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Surface treatment technologies for wear resistance increasing of 42CrMo4 steel.
Popis výsledku v původním jazyce
The present study was directed to investigate the mechanical and tribological properties of 42CrMo4 (CSN 41 5142.3) steel, which was chemical?heat treated by the technologies of tenifer, manganese phosphate and plasma nitriding combining with blackening.Plasma nitriding was carried out for the samples under different condition of gas mixture under temperature of 480?C (plasma sputtering) and 500?C (plasma nitriding process) for 10h. Besides determining the microhardness (HV 0.05), surface hardness, andmicrostructure, this paper is also focused in the field of wear resistance evaluation and friction coefficient of these surface treatments. Based on ?ball on flat? test, calotest, and profile observation, it was found that tenifer technology is suitableto increase the wear resistance, and manganese phosphate improved clearly not only wear resistance but also friction coefficient, which can be usable for weapon production.
Název v anglickém jazyce
Surface treatment technologies for wear resistance increasing of 42CrMo4 steel.
Popis výsledku anglicky
The present study was directed to investigate the mechanical and tribological properties of 42CrMo4 (CSN 41 5142.3) steel, which was chemical?heat treated by the technologies of tenifer, manganese phosphate and plasma nitriding combining with blackening.Plasma nitriding was carried out for the samples under different condition of gas mixture under temperature of 480?C (plasma sputtering) and 500?C (plasma nitriding process) for 10h. Besides determining the microhardness (HV 0.05), surface hardness, andmicrostructure, this paper is also focused in the field of wear resistance evaluation and friction coefficient of these surface treatments. Based on ?ball on flat? test, calotest, and profile observation, it was found that tenifer technology is suitableto increase the wear resistance, and manganese phosphate improved clearly not only wear resistance but also friction coefficient, which can be usable for weapon production.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
KA - Vojenství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Materiály a technologie ve výrobě speciální techniky
ISBN
978-80-7231-999-2
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
25-30
Název nakladatele
UO Brno, Czech Republic
Místo vydání
Brno
Místo konání akce
Brno
Datum konání akce
20. 5. 2015
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—