Material Analysis Of Cracked 12,7 mm x 99 mm Cartridge Cases
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60162694%3AG43__%2F15%3A00531630" target="_blank" >RIV/60162694:G43__/15:00531630 - isvavai.cz</a>
Výsledek na webu
<a href="http://vavtest.unob.cz/registr" target="_blank" >http://vavtest.unob.cz/registr</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Material Analysis Of Cracked 12,7 mm x 99 mm Cartridge Cases
Popis výsledku v původním jazyce
The paper is focused on the material analysis of 12,7 mm x 99 mm brass cartridge cases of two producers. The reason for complete material analyses was about 40% longitudinal cracking of different lengths of cartridge cases after shoting. The material analysis of above mentioned brass cartridge cases was performed using the laboratory equipment of Department of Engeneering and consisted of following steps: sampling and sample preparation, microstructure evaluation using the light microscope Olympus GX 51, wall thickness measuring of cartridge cases, hardness measuring using the LECO LV800AT, microhardness measuring using the microhardness tester LECO LM247AT, chemical composition measuring using the X-ray spectrometer Delta. The material analysis showed increased hardness, differences of the microstructure and chemical composition, which causes longitudinal cracking of brass cartridge cases when fired.
Název v anglickém jazyce
Material Analysis Of Cracked 12,7 mm x 99 mm Cartridge Cases
Popis výsledku anglicky
The paper is focused on the material analysis of 12,7 mm x 99 mm brass cartridge cases of two producers. The reason for complete material analyses was about 40% longitudinal cracking of different lengths of cartridge cases after shoting. The material analysis of above mentioned brass cartridge cases was performed using the laboratory equipment of Department of Engeneering and consisted of following steps: sampling and sample preparation, microstructure evaluation using the light microscope Olympus GX 51, wall thickness measuring of cartridge cases, hardness measuring using the LECO LV800AT, microhardness measuring using the microhardness tester LECO LM247AT, chemical composition measuring using the X-ray spectrometer Delta. The material analysis showed increased hardness, differences of the microstructure and chemical composition, which causes longitudinal cracking of brass cartridge cases when fired.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
KA - Vojenství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Armament and technics of land forces 2015
ISBN
978-80-8040-518-2
ISSN
—
e-ISSN
—
Počet stran výsledku
9
Strana od-do
-1
Název nakladatele
Akademie ozbrojených sil gen. M. R. Štefánika
Místo vydání
Liptovský Mikuláš
Místo konání akce
Liptovský Mikuláš, Slovenská republika
Datum konání akce
12. 11. 2015
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—