Influence of Initial Carbon Concentration on Nitride Layers

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60162694%3AG43__%2F15%3A00531958" target="_blank" >RIV/60162694:G43__/15:00531958 - isvavai.cz</a>

Výsledek na webu

<a href="http://vavtest.unob.cz/registr" target="_blank" >http://vavtest.unob.cz/registr</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Initial Carbon Concentration on Nitride Layers

Popis výsledku v původním jazyce

The properties of plasma nitride layer are determined except technological parameters by chemical composition and structure of steel. Experiments were carried out on ARMOX 500T steel.Firstly, the samples of steel were carburized and isothermal hardened. After quenching the course of microhardness was measured from surface to the core of material. Samples were cutted off on metallographic saw and subsequently grinded from the surface to the core of material. All depths of grinded surface from surface to the core were exactly defined. The chemical composition was verified in each prepared samples. Samples with changeable content of carbon were nitrided by plasma nitriding technology. All properties of plasma nitriding layers were evaluated.

Název v anglickém jazyce

Influence of Initial Carbon Concentration on Nitride Layers

Popis výsledku anglicky

The properties of plasma nitride layer are determined except technological parameters by chemical composition and structure of steel. Experiments were carried out on ARMOX 500T steel.Firstly, the samples of steel were carburized and isothermal hardened. After quenching the course of microhardness was measured from surface to the core of material. Samples were cutted off on metallographic saw and subsequently grinded from the surface to the core of material. All depths of grinded surface from surface to the core were exactly defined. The chemical composition was verified in each prepared samples. Samples with changeable content of carbon were nitrided by plasma nitriding technology. All properties of plasma nitriding layers were evaluated.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

KA - Vojenství

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

15

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

5

Strana od-do

889-893

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—