Plasma Nitriding of Martensitic Stainless Steel X12Cr13

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60162694%3AG43__%2F16%3A00532914" target="_blank" >RIV/60162694:G43__/16:00532914 - isvavai.cz</a>

Výsledek na webu

<a href="http://vavtest.unob.cz/registr" target="_blank" >http://vavtest.unob.cz/registr</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

slovinština

Název v původním jazyce

Plazmová nitridácia koroziivzdornej ocele X12Cr13

Popis výsledku v původním jazyce

Plazmová nitridácia je výborné termochemické spracovanie používané v mnohých technických aplikáciách ako finálna operácia pre zlepšenie mechanických, tribologických a koróznych vlastností ocele. Príspevok je zameraný na plazmovú nitridáciu martenzitickej koroziivzdornej ocele X12Cr13. Skúmaný bol vplyv chemického zloženia ocele na hrúbku a mikrotvrdosť nitridovaných vrstiev. Proces plazmovej nitridácie bol vykonaný za použitia dvoch stupňov plazmovej nitridácie. Po čistiacej procedúre pri 515 °C počas 45 min bol prvý stupeň plazmovej nitridácie vykonaný pri 520 °C počas 16 hodín, a následne druhá fáza nitridácie pri 525 ° C, počas 4 hodín. Mikroštruktúra a mechanické vlastnosti nitridovaných vrstiev boli študované za použitia GDOES spektrometrie, optickej mikroskopie a merania tvrdosti. Hĺbky plazmovo nitridovaných vrstiev boli hodnotené pomocou merania mikrotvrdosti v priečnom reze. Mikrotvrdosti a povrchová tvrdosť uvedených vzoriek sa výrazne zvýšili. Vplyv difuzivity a podmienok plazmovej nitridácie na hĺbku nitridovanej vrstvy bol komplexne posúdený. Merania ukázali, že obsah legujúcich prvkov má významný vplyv na vytváranie plazmového nitridovanej vrstvy.

Název v anglickém jazyce

Plasma Nitriding of Martensitic Stainless Steel X12Cr13

Popis výsledku anglicky

Plasma nitriding is a great thermochemical treatment, widely used in many technical applications as a final operation to improve the mechanical, tribological and corrosion properties of steel. This paper is focused in plasma nitriding treatment of martensitic stainless steel X12Cr13. The influence of chemical composition of steel on thickness and microhardness of nitrided layers were investigated. The plasma nitriding process was performed using two stage nitriding procedures. After plasma cleaning procedure at 515 °C for 45 min was the first stage nitriding procedure performed at 520°C for 16 hours and followed by second stage of nitriding procedure performed at 525°C for 4 hours. The microstructure and mechanical properties of nitrided layers were studied using GDOES spectrometry, optical microscopy, and hardness testing. The depths of the plasma nitride layers were also estimated using cross-sectional microhardness profiles measuring. Microhardness and surface hardness of mentioned samples were significantly increased. The influence of diffusivity and plasma nitriding conditions on the nitride layers depth was comprehensively assessed. The measurements have shown that the content of alloying elements has a significant influence on the creation of plasma nitride layer.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Vrstvy a povlaky 2016

ISBN

978-80-972133-1-2

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

89-93

Název nakladatele

M-PRESS s.r.o.

Místo vydání

Trenčianska Teplá

Místo konání akce

Rožnov pod Radhošem

Datum konání akce

17. 10. 2016

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—