Creep behaviour and microstructure of 2.25%Cr1.6%W steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60193247%3A_____%2F09%3AUJP1378C" target="_blank" >RIV/60193247:_____/09:UJP1378C - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/09:00332669

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Creep behaviour and microstructure of 2.25%Cr1.6%W steel

Popis výsledku v původním jazyce

Conventional 2.25%Cr1%Mo steel has been greatly improved by the substitution of almost all of the 1%Mo by 1.6%W. The improved material has been standardised as T23 steel (Fe-2.25Cr-1.6W-0.25V-0.05Nb-0.07C). The present investigation was conducted on T23steel in an effort to obtain more complete description and understanding of the role of microstructure evolution and deformation processes in high temperature creep. Constant load tensile creep tests were carried out in the temperature range of 500-650 degrees C at stresses ranged from 50 to 400 MPa. The results of an extensive TEM analysis program to investigate microstructure evolution as function of temperature are described and compared with the thermodynamic calculations using the software packageThermo-Calc.

Název v anglickém jazyce

Creep behaviour and microstructure of 2.25%Cr1.6%W steel

Popis výsledku anglicky

Conventional 2.25%Cr1%Mo steel has been greatly improved by the substitution of almost all of the 1%Mo by 1.6%W. The improved material has been standardised as T23 steel (Fe-2.25Cr-1.6W-0.25V-0.05Nb-0.07C). The present investigation was conducted on T23steel in an effort to obtain more complete description and understanding of the role of microstructure evolution and deformation processes in high temperature creep. Constant load tensile creep tests were carried out in the temperature range of 500-650 degrees C at stresses ranged from 50 to 400 MPa. The results of an extensive TEM analysis program to investigate microstructure evolution as function of temperature are described and compared with the thermodynamic calculations using the software packageThermo-Calc.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

CREEP & FRACTURE IN HIGH TEMPERATURE COMPONENTS: DESIGN & LIFE ASSESSMENT ISSUES, PROCEEDINGS

ISBN

978-1-60595-005-1

ISSN

—

e-ISSN

—

Počet stran výsledku

9

Strana od-do

—

Název nakladatele

DESTECH PUBLICATIONS, INC

Místo vydání

Lancaster, Pennsylvania, USA

Místo konání akce

Zurich, Switzerland

Datum konání akce

21. 4. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—