Microstructure and mechanical properties of Ti-35Nb-6Ta alloy after thermomechanical treatment

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60193247%3A_____%2F12%3AUJP1463F" target="_blank" >RIV/60193247:_____/12:UJP1463F - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21220/12:00203169 RIV/00216208:11320/12:10128527

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S104458031200037X" target="_blank" >http://www.sciencedirect.com/science/article/pii/S104458031200037X</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.matchar.2012.02.012" target="_blank" >10.1016/j.matchar.2012.02.012</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructure and mechanical properties of Ti-35Nb-6Ta alloy after thermomechanical treatment

Popis výsledku v původním jazyce

"The influence of thermo-mechanical treatment on microstructure and mechanical properties of T-35Nb-6Ta has been studied. The thermo-mechanical treatment was chosen to correspond to the production of wire with suitable mechanical properties for dental implants. After casting the alloy was hot forged (700?900 °C), solution treated (850 °C/30 min, water quenched) and cold swaged (reductions up to 91%). The annealing (700 °C/3 h/furnace) or aging (450 °C/8 h/furnace) was used as final heat treatment. The microstructure was studied by using light microscopy, scanning electronmicroscopy, transmission electron microscopy and XRD analysis. Cold swaging introduces microstructure consisting of highly deformed ?-phase grains with dislocation tangles and twins,which ensures high tensile strength about 820 MPa, lowYoung's modulus (~50 GPa) and good ductility ~10%. Subsequent aging increases tensile strength (1000 MPa) as well as Young's modulus (75 GPa) without diminishing ductility. Annealing at

Název v anglickém jazyce

Microstructure and mechanical properties of Ti-35Nb-6Ta alloy after thermomechanical treatment

Popis výsledku anglicky

"The influence of thermo-mechanical treatment on microstructure and mechanical properties of T-35Nb-6Ta has been studied. The thermo-mechanical treatment was chosen to correspond to the production of wire with suitable mechanical properties for dental implants. After casting the alloy was hot forged (700?900 °C), solution treated (850 °C/30 min, water quenched) and cold swaged (reductions up to 91%). The annealing (700 °C/3 h/furnace) or aging (450 °C/8 h/furnace) was used as final heat treatment. The microstructure was studied by using light microscopy, scanning electronmicroscopy, transmission electron microscopy and XRD analysis. Cold swaging introduces microstructure consisting of highly deformed ?-phase grains with dislocation tangles and twins,which ensures high tensile strength about 820 MPa, lowYoung's modulus (~50 GPa) and good ductility ~10%. Subsequent aging increases tensile strength (1000 MPa) as well as Young's modulus (75 GPa) without diminishing ductility. Annealing at

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/2A-2TP1%2F073" target="_blank" >2A-2TP1/073: Výzkum materiálových a užitných vlastností moderních vysokolegovaných stabilních beta-titanových slitin a vývoj technologie jejich výroby práškovou metalurgií.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Characterization

ISSN

1044-5803

e-ISSN

—

Svazek periodika

66

Číslo periodika v rámci svazku

April 2012

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

8

Strana od-do

75-82

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—