Strukture Stability of Ni-Base and Co-Base Alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60193247%3A_____%2F13%3AUJP1454A" target="_blank" >RIV/60193247:_____/13:UJP1454A - isvavai.cz</a>

Výsledek na webu

<a href="http://www.scientific.net/" target="_blank" >http://www.scientific.net/</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Strukture Stability of Ni-Base and Co-Base Alloys

Popis výsledku v původním jazyce

This article summarises results of structure stability investigation of cast Ni-base and Co-base alloys after prolonged high temperature exposure at 900-1100 °C. Cast Ni(Co)-Cr-W-C alloys are resistant to high-temperature corrosion, due to high chromiumcontent. Their heat resistance is caused by presence of carbides, which are stable at very high temperatures. Carbides precipitate in shape of large plate-like particles or carbide eutectics at casting cell boundaries, thus forming carbide skeleton of the alloy. Carbide morphology and temperature stability depends on chemical composition of the alloy, e.g. carbide content, type and content of carbide-forming elements. Microstructure changes were evaluated by stereological analysis and X ray-spectral microanalysis.

Název v anglickém jazyce

Strukture Stability of Ni-Base and Co-Base Alloys

Popis výsledku anglicky

This article summarises results of structure stability investigation of cast Ni-base and Co-base alloys after prolonged high temperature exposure at 900-1100 °C. Cast Ni(Co)-Cr-W-C alloys are resistant to high-temperature corrosion, due to high chromiumcontent. Their heat resistance is caused by presence of carbides, which are stable at very high temperatures. Carbides precipitate in shape of large plate-like particles or carbide eutectics at casting cell boundaries, thus forming carbide skeleton of the alloy. Carbide morphology and temperature stability depends on chemical composition of the alloy, e.g. carbide content, type and content of carbide-forming elements. Microstructure changes were evaluated by stereological analysis and X ray-spectral microanalysis.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FR-TI1%2F095" target="_blank" >FR-TI1/095: Výzkum a vývoj materiálů vhodných pro použití v prostředí tekuté skloviny, vývoj technologií přesného lití nových typů odlitků vysoce tepelně a mechanicky namáhaných.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science Forum

ISSN

0255-5476

e-ISSN

—

Svazek periodika

782

Číslo periodika v rámci svazku

2013

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

6

Strana od-do

431-436

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—