Mechanical Properties and Microstructure of IN713LC Nickel Superalloy Castings

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60193247%3A_____%2F13%3AUJP1498A" target="_blank" >RIV/60193247:_____/13:UJP1498A - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical Properties and Microstructure of IN713LC Nickel Superalloy Castings

Popis výsledku v původním jazyce

IN713LC is a nickel-base casting alloy developed for applications requiring high strength at elevated temperatures. Its balanced composition provides a good combination of tensile and creep-rupture properties as a result of gamma-prime strengthening enhanced by solid solution and grain-boundary strengthening. IN713LC alloy performs a good castability. Castings are used in as-cast state, without heat treatment.Currently, this alloy is used widely, for example, for manufacturing of turbine wheels in turbochargers. Recently, customers demand the production of increasingly larger parts of impellers than before. This requirement has resulted in a greater weight of castings and thus different conditions during solidifying and cooling of the castings. Therefore modified castings microstructure arises.When approving the castings, mechanical values are measured by tensile test on test bodies made from the centres of the castings. These test bodies often exhibit lower values than required, in pa

Název v anglickém jazyce

Mechanical Properties and Microstructure of IN713LC Nickel Superalloy Castings

Popis výsledku anglicky

IN713LC is a nickel-base casting alloy developed for applications requiring high strength at elevated temperatures. Its balanced composition provides a good combination of tensile and creep-rupture properties as a result of gamma-prime strengthening enhanced by solid solution and grain-boundary strengthening. IN713LC alloy performs a good castability. Castings are used in as-cast state, without heat treatment.Currently, this alloy is used widely, for example, for manufacturing of turbine wheels in turbochargers. Recently, customers demand the production of increasingly larger parts of impellers than before. This requirement has resulted in a greater weight of castings and thus different conditions during solidifying and cooling of the castings. Therefore modified castings microstructure arises.When approving the castings, mechanical values are measured by tensile test on test bodies made from the centres of the castings. These test bodies often exhibit lower values than required, in pa

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FR-TI3%2F055" target="_blank" >FR-TI3/055: Výzkum a vývoj technologií přesného lití nových typů odlitků ze superslitin na bázi niklu pro odlitky rotorových částí turbodmychadel a letecké turbíny</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Conference METAL 2013 Proceedings

ISBN

978-80-87294-31-4

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

TANGER, Ltd.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

1. 1. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—