The Effect of Solution Treatment Temperature on Plastic Deformation and Fracture Mechanisms of Beta-Titanium Alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60193247%3A_____%2F17%3AN0000009" target="_blank" >RIV/60193247:_____/17:N0000009 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.scientific.net/SSP.270.218" target="_blank" >https://www.scientific.net/SSP.270.218</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.270.218" target="_blank" >10.4028/www.scientific.net/SSP.270.218</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The Effect of Solution Treatment Temperature on Plastic Deformation and Fracture Mechanisms of Beta-Titanium Alloy

Popis výsledku v původním jazyce

The beta-titanium alloys are used mainly in bioapplications for artificial joints and other implants. They posses interesting properties such as, high corrosion resistance, low Young’s modulus, good plasticity or superelasticity etc. In this work the effect of solution treatment temperature on deformation and fracture properties has been studied. The alloy Ti-35Nb-2Zr was processed via powder metallurgy process (cold isostatic pressing, sintering and subsequent swaging). Swaged alloy was annealed at 800, 850, 900, 950 and 1000 °C. Tensile tests have been performed on such heat treated specimens and the fracture surface has been studied in correlation with microstructure. With increasing annealing temperature both tensile strength (from 925 MPa to 990 MPa) and elongation (from 13 to 25 %) increased where the maximum values were obtained for 900 °C annealed specimens and subsequently slight decrease has been observed. The simultaneous increase of strength and elongation was attached to change of deformation mechanisms which was described by studying fracture surfaces and microstructure of deformed (tensile tested) specimens.

Název v anglickém jazyce

The Effect of Solution Treatment Temperature on Plastic Deformation and Fracture Mechanisms of Beta-Titanium Alloy

Popis výsledku anglicky

The beta-titanium alloys are used mainly in bioapplications for artificial joints and other implants. They posses interesting properties such as, high corrosion resistance, low Young’s modulus, good plasticity or superelasticity etc. In this work the effect of solution treatment temperature on deformation and fracture properties has been studied. The alloy Ti-35Nb-2Zr was processed via powder metallurgy process (cold isostatic pressing, sintering and subsequent swaging). Swaged alloy was annealed at 800, 850, 900, 950 and 1000 °C. Tensile tests have been performed on such heat treated specimens and the fracture surface has been studied in correlation with microstructure. With increasing annealing temperature both tensile strength (from 925 MPa to 990 MPa) and elongation (from 13 to 25 %) increased where the maximum values were obtained for 900 °C annealed specimens and subsequently slight decrease has been observed. The simultaneous increase of strength and elongation was attached to change of deformation mechanisms which was described by studying fracture surfaces and microstructure of deformed (tensile tested) specimens.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Solid State Phenomena

ISBN

—

ISSN

1662-9779

e-ISSN

—

Počet stran výsledku

6

Strana od-do

218-223

Název nakladatele

scientific.net

Místo vydání

Zurich, CH

Místo konání akce

Mariánské Lázně, Czech Republic

Datum konání akce

6. 6. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—