Influence of high temperature overheating to microstructure of degraded steel super 304H
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60193247%3A_____%2F18%3AN0000001" target="_blank" >RIV/60193247:_____/18:N0000001 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of high temperature overheating to microstructure of degraded steel super 304H
Popis výsledku v původním jazyce
This paper documents the microstructure changes of steel SUPER 304H caused by high temperature overheating (1140 °C, 15 hours). The experimental material was firstly isothermally laboratory exposed about 30,000 hours at temperature 650 °C and then subject to high temperature overheating. Main focus was given to microstructural changes and precipitation processes. Paper summarized influence of those changes to practical applicability of steel SUPER 304H for ultra-super critical (USC) coal power plants. Base material, laboratory expose state and overheated state were compared. Combination of color etching and optical microscopy method, electron scanning microscopy and energy dispersive spectroscopy analysis was used for comparison.
Název v anglickém jazyce
Influence of high temperature overheating to microstructure of degraded steel super 304H
Popis výsledku anglicky
This paper documents the microstructure changes of steel SUPER 304H caused by high temperature overheating (1140 °C, 15 hours). The experimental material was firstly isothermally laboratory exposed about 30,000 hours at temperature 650 °C and then subject to high temperature overheating. Main focus was given to microstructural changes and precipitation processes. Paper summarized influence of those changes to practical applicability of steel SUPER 304H for ultra-super critical (USC) coal power plants. Base material, laboratory expose state and overheated state were compared. Combination of color etching and optical microscopy method, electron scanning microscopy and energy dispersive spectroscopy analysis was used for comparison.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2018 - 27th International Conference on Metallurgy and Materials, Conference Proceedings 2018
ISBN
978-80-87294-84-0
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
553-558
Název nakladatele
TANGER Ltd., Ostrava
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
23. 5. 2018
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—