Abrasive wear of high chromium Fe-Cr-C hardfacing alloys

Popis výsledku v původním jazyce

Weld deposits are one of most used economical ways of wear resistance increase. The study compares overlay material welded-on characteristics and abrasive wear resistance. The research has been carried out using hardfacing alloys reinforced with primarychromium carbides and complex carbides. The overlay material was deposited on the low-carbon steel S235JR using the gas metal arc welding (GMAW) method. Four different commercial overlay materials were studied in term of the microstructure effect. Abrasion wear testing was carried out using the abrasive cloth of grit 120 according to CSN 01 5084. Microstructure characterization and surface analysis were made using optical and scanning electron microscopy. Results illustrate the significant effect of primary carbides on abrasive wear resistance of weld deposits.

Název v anglickém jazyce

Abrasive wear of high chromium Fe-Cr-C hardfacing alloys

Popis výsledku anglicky

Weld deposits are one of most used economical ways of wear resistance increase. The study compares overlay material welded-on characteristics and abrasive wear resistance. The research has been carried out using hardfacing alloys reinforced with primarychromium carbides and complex carbides. The overlay material was deposited on the low-carbon steel S235JR using the gas metal arc welding (GMAW) method. Four different commercial overlay materials were studied in term of the microstructure effect. Abrasion wear testing was carried out using the abrasive cloth of grit 120 according to CSN 01 5084. Microstructure characterization and surface analysis were made using optical and scanning electron microscopy. Results illustrate the significant effect of primary carbides on abrasive wear resistance of weld deposits.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Research in Agricultural Engineering (Zemědělská technika)

ISSN

1212-9151

e-ISSN

—

Svazek periodika

54

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—