The effect of heat treatment on the microstructure, hardness and abrasive wear resistance of high chromium hardfacing
Popis výsledku v původním jazyce
The effect of destabilization heat treatment on the microstructure, hardness, fracture toughness and abrasive wear resistance of high chromium hardfacing was investigated. The results from the study shows that the hardness, fracture toughness and abrasive wear resistance are influenced by temperature of destabilization heat treatment and air and furnace cooling conditions respectively. Destabilization treatment of materials by furnace cooling caused higher secondary carbides in the dendritic austenite whilst by air cooling showed smaller particles of secondary carbide. Also, it was found that destabilization temperature at 1000°C improves hardness compared with hardfacing after weld depositing. The study, however, indicated that Palmqvist fracture toughness method is a useful technique for measuring the fracture toughness of high chromium hardfacing compared to Vicker?s hardness method.
Název v anglickém jazyce
The effect of heat treatment on the microstructure, hardness and abrasive wear resistance of high chromium hardfacing
Popis výsledku anglicky
The effect of destabilization heat treatment on the microstructure, hardness, fracture toughness and abrasive wear resistance of high chromium hardfacing was investigated. The results from the study shows that the hardness, fracture toughness and abrasive wear resistance are influenced by temperature of destabilization heat treatment and air and furnace cooling conditions respectively. Destabilization treatment of materials by furnace cooling caused higher secondary carbides in the dendritic austenite whilst by air cooling showed smaller particles of secondary carbide. Also, it was found that destabilization temperature at 1000°C improves hardness compared with hardfacing after weld depositing. The study, however, indicated that Palmqvist fracture toughness method is a useful technique for measuring the fracture toughness of high chromium hardfacing compared to Vicker?s hardness method.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/TA01010192" target="_blank" >TA01010192: Výzkum a vývoj otěruvzdorných materiálů a technologií pro jejich využití u zemědělských strojů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Research in Agricultural Engineering (Zemědělská technika)
ISSN
1212-9151
e-ISSN
—
Svazek periodika
59
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
6
Strana od-do
23-28
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—