Quasi Static Tests of Adhesive Bonds of Alloy AlCu4 Mg
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41310%2F15%3A68410" target="_blank" >RIV/60460709:41310/15:68410 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Quasi Static Tests of Adhesive Bonds of Alloy AlCu4 Mg
Popis výsledku v původním jazyce
An application of an adhesive bonding technology is limited by cyclic loading of an adhesive bond. The aim of the experiment is to clarify a fatigue behaviour (low-cyclic tests of the fatigue) of four structural two-component epoxy adhesives applied to an alloy AlCu4Mg. The aim of the research was to evaluate a service life of the adhesive bond in terms of its fatigue stressing at the quasi static shear test. From that reason values of a passing loading for low- cyclic fatigue test were chosen for tested adhesives, i.e. 25 %, 50 % and 75 % from a reference value of a maximum force gained at the static test according to CSN EN 1465. The critical value at the low-cyclic fatigue test was deter- mined from the experiment results for the adhesive bond as 75%. Most of the adhesive bonds did not reach 100 cycles at this value. It is obvious from the results that the considerable change of the adhesive bond strength did not occur after 100 cycles at the passing loading corresponding t
Název v anglickém jazyce
Quasi Static Tests of Adhesive Bonds of Alloy AlCu4 Mg
Popis výsledku anglicky
An application of an adhesive bonding technology is limited by cyclic loading of an adhesive bond. The aim of the experiment is to clarify a fatigue behaviour (low-cyclic tests of the fatigue) of four structural two-component epoxy adhesives applied to an alloy AlCu4Mg. The aim of the research was to evaluate a service life of the adhesive bond in terms of its fatigue stressing at the quasi static shear test. From that reason values of a passing loading for low- cyclic fatigue test were chosen for tested adhesives, i.e. 25 %, 50 % and 75 % from a reference value of a maximum force gained at the static test according to CSN EN 1465. The critical value at the low-cyclic fatigue test was deter- mined from the experiment results for the adhesive bond as 75%. Most of the adhesive bonds did not reach 100 cycles at this value. It is obvious from the results that the considerable change of the adhesive bond strength did not occur after 100 cycles at the passing loading corresponding t
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JR - Ostatní strojírenství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Svazek periodika
15
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
5
Strana od-do
694-698
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—