Modification of veneers by lamination and steaming for the purpose of increasing 3D moldability

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41320%2F14%3A64965" target="_blank" >RIV/60460709:41320/14:64965 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Modification of veneers by lamination and steaming for the purpose of increasing 3D moldability

Popis výsledku v původním jazyce

The focus of this work was to determine the 3D moldability of veneers on circular test pieces treated with steam plastification. These results were compared with results acquired from pieces laminated with three different types of laminating foils with thicknesses of 80, 100, and 125 ?m before proper 3D molding. The purpose of test piece lamination was to change the degree of pre-stress and move the neutral plane into the laminating foil, which actually works as a flange. Results acquired from sets of test pieces modified by steam plastification and lamination were compared with the results acquired for the set of test pieces without any treatment. To determine the effects of wood type, the results obtained with beech wood of 0.5-mm thickness were compared with the results acquired from birch wood of 0.5-mm thickness using two types of spherical stamping tools with 20-mm and 40-mm diameters for molding the test pieces. The final examined characteristics were the means of attachment of

Název v anglickém jazyce

Modification of veneers by lamination and steaming for the purpose of increasing 3D moldability

Popis výsledku anglicky

The focus of this work was to determine the 3D moldability of veneers on circular test pieces treated with steam plastification. These results were compared with results acquired from pieces laminated with three different types of laminating foils with thicknesses of 80, 100, and 125 ?m before proper 3D molding. The purpose of test piece lamination was to change the degree of pre-stress and move the neutral plane into the laminating foil, which actually works as a flange. Results acquired from sets of test pieces modified by steam plastification and lamination were compared with the results acquired for the set of test pieces without any treatment. To determine the effects of wood type, the results obtained with beech wood of 0.5-mm thickness were compared with the results acquired from birch wood of 0.5-mm thickness using two types of spherical stamping tools with 20-mm and 40-mm diameters for molding the test pieces. The final examined characteristics were the means of attachment of

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JP - Průmyslové procesy a zpracování

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

BioResources

ISSN

1930-2126

e-ISSN

—

Svazek periodika

9

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

11

Strana od-do

7141-7151

Kód UT WoS článku

000345396900108

EID výsledku v databázi Scopus

—