Influence of densification on bending strength of laminated beech wood
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41320%2F15%3A66342" target="_blank" >RIV/60460709:41320/15:66342 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.15376/biores.10.1.1506-1518" target="_blank" >http://dx.doi.org/10.15376/biores.10.1.1506-1518</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.15376/biores.10.1.1506-1518" target="_blank" >10.15376/biores.10.1.1506-1518</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of densification on bending strength of laminated beech wood
Popis výsledku v původním jazyce
This paper reports the influence of densification and cyclic loading on the bending strength of laminated beech (Fagus sylvatica L.). There are many studies dealing with the bending strength of solid or laminated wood; however, densification is much lessexplored with respect to its use in the production of laminated wood. Laminated beech wood was loaded by three different numbers of cycles (1000, 2000, and 3000 cycles). Bending strength values of the cyclically loaded laminated wood were compared withthat of cyclically non-loaded laminated wood. The laminated wood was formed by a combination of densified and non-densified veneers, as well as polyvinyl cholride (PVC) fabric. The results show that the laminated wood consisting of densified and non-densified veneers, eventually with PVC film included, reached the higher values of bending strength in comparison with the traditional composition consisting of non-densified veneers. Densification had a strong impact on the bending strength,
Název v anglickém jazyce
Influence of densification on bending strength of laminated beech wood
Popis výsledku anglicky
This paper reports the influence of densification and cyclic loading on the bending strength of laminated beech (Fagus sylvatica L.). There are many studies dealing with the bending strength of solid or laminated wood; however, densification is much lessexplored with respect to its use in the production of laminated wood. Laminated beech wood was loaded by three different numbers of cycles (1000, 2000, and 3000 cycles). Bending strength values of the cyclically loaded laminated wood were compared withthat of cyclically non-loaded laminated wood. The laminated wood was formed by a combination of densified and non-densified veneers, as well as polyvinyl cholride (PVC) fabric. The results show that the laminated wood consisting of densified and non-densified veneers, eventually with PVC film included, reached the higher values of bending strength in comparison with the traditional composition consisting of non-densified veneers. Densification had a strong impact on the bending strength,
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
BioResources
ISSN
1930-2126
e-ISSN
—
Svazek periodika
10
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
13
Strana od-do
1506-1518
Kód UT WoS článku
000351941000121
EID výsledku v databázi Scopus
—