Efficacy of Hydrophobic Coatings in Protecting Oak Wood Surfaces during Accelerated Weathering

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41320%2F17%3A74915" target="_blank" >RIV/60460709:41320/17:74915 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.3390/coatings7100172" target="_blank" >http://dx.doi.org/10.3390/coatings7100172</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/coatings7100172" target="_blank" >10.3390/coatings7100172</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Efficacy of Hydrophobic Coatings in Protecting Oak Wood Surfaces during Accelerated Weathering

Popis výsledku v původním jazyce

The durability of transparent coatings applied to an oak wood exterior is relatively low due to its anatomic structure and chemical composition. Enhancement of the protection of oak wood against weathering using transparent hydrophobic coatings is presented in this study. Oak wood surfaces were modified using UV-stabilizers, hindered amine light stabilizer (HALS), and ZnO and TiO2 nanoparticles before the application of a commercial hydrophobic topcoat. A transparent oil-based coating was used as a control coating system. The artificial weathering test lasted 6 weeks and colour, gloss, and contact angle changes were regularly evaluated during this period. The changes in the microscopic structure were studied with confocal laser scanning microscopy. The results proved limited durability against weathering of both tested hydrophobic coatings. The formation of micro-cracks causing the leaching of degraded wood compounds and discolouration of oak wood were observed after 1 or 3 weeks of the weathering te

Název v anglickém jazyce

Efficacy of Hydrophobic Coatings in Protecting Oak Wood Surfaces during Accelerated Weathering

Popis výsledku anglicky

The durability of transparent coatings applied to an oak wood exterior is relatively low due to its anatomic structure and chemical composition. Enhancement of the protection of oak wood against weathering using transparent hydrophobic coatings is presented in this study. Oak wood surfaces were modified using UV-stabilizers, hindered amine light stabilizer (HALS), and ZnO and TiO2 nanoparticles before the application of a commercial hydrophobic topcoat. A transparent oil-based coating was used as a control coating system. The artificial weathering test lasted 6 weeks and colour, gloss, and contact angle changes were regularly evaluated during this period. The changes in the microscopic structure were studied with confocal laser scanning microscopy. The results proved limited durability against weathering of both tested hydrophobic coatings. The formation of micro-cracks causing the leaching of degraded wood compounds and discolouration of oak wood were observed after 1 or 3 weeks of the weathering te

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Coatings

ISSN

2079-6412

e-ISSN

—

Svazek periodika

7

Číslo periodika v rámci svazku

10

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

15

Strana od-do

1-15

Kód UT WoS článku

000414849800021

EID výsledku v databázi Scopus

—