Evolution of crystalline phases during feed-to-glass conversion

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F01%3A00004162" target="_blank" >RIV/60461373:22310/01:00004162 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Evolution of crystalline phases during feed-to-glass conversion
Popis výsledku v původním jazyce
Simulated high-level waste (HLW) feed, prepared with co-precipitated Fe, Ni, Cr , and Mn hydroxides to simulate the formation of spinel, was heated up at temperature-increase rates believed to be close to those the feed experiences in the HLW glass melter. Decomposition, melting, and dissolution of the feed components (such as nitrates and silica) and the formation of intermediate crystalline phases were observed and characterized.
Název v anglickém jazyce
Evolution of crystalline phases during feed-to-glass conversion
Popis výsledku anglicky
Simulated high-level waste (HLW) feed, prepared with co-precipitated Fe, Ni, Cr , and Mn hydroxides to simulate the formation of spinel, was heated up at temperature-increase rates believed to be close to those the feed experiences in the HLW glass melter. Decomposition, melting, and dissolution of the feed components (such as nitrates and silica) and the formation of intermediate crystalline phases were observed and characterized.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—

Rok uplatnění
2001
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)