The corrosion of coated and uncoated Mo and uncoated MoZrO2 in glass melts under a.c. loading

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F01%3A00004383" target="_blank" >RIV/60461373:22310/01:00004383 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The corrosion of coated and uncoated Mo and uncoated MoZrO2 in glass melts under a.c. loading

Popis výsledku v původním jazyce

Three molybdenum based materials were exposed to three commercial glass melts under alternating current loading. The most significant deviation to lower corrosion could be found for material doped by 5% ZrO2 in green bottle glass. Retardation of intercristalline corrosion by the particles of the dopant may be responsible for the behaviour. Sibor (Si-B) coated molybdenum was also tested in borosilicate glass melts. After an initial period of strong dissolution and bubble formation the corrosion rate decreased and became lower than at three uncoated molybdenum materials. Presumably the preferential reaction of Si and B over the initial period is responsible for this effect.

Název v anglickém jazyce

The corrosion of coated and uncoated Mo and uncoated MoZrO2 in glass melts under a.c. loading

Popis výsledku anglicky

Three molybdenum based materials were exposed to three commercial glass melts under alternating current loading. The most significant deviation to lower corrosion could be found for material doped by 5% ZrO2 in green bottle glass. Retardation of intercristalline corrosion by the particles of the dopant may be responsible for the behaviour. Sibor (Si-B) coated molybdenum was also tested in borosilicate glass melts. After an initial period of strong dissolution and bubble formation the corrosion rate decreased and became lower than at three uncoated molybdenum materials. Presumably the preferential reaction of Si and B over the initial period is responsible for this effect.

Druh

D - Stať ve sborníku

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings 15. Internat. Plansee Seminar

ISBN

neuveden

ISSN

—

e-ISSN

—

Počet stran výsledku

12

Strana od-do

217-228

Název nakladatele

Neuveden

Místo vydání

Neuvedeno

Místo konání akce

Reutte, Austria

Datum konání akce

1. 1. 2001

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—