Influence of B, Al, Ga, In on Composition of Bi(Pb)SrCaCuO System

Popis výsledku v původním jazyce

Samples Bi1.8-xAxPb0.26Sr2Ca2Cu3Oy were prepared to systematically examine phase formation due to concentrations x = 0 - 0.5 of B, Al, Ga and In in the range. All samples were mixed phases of 2212 and 2223. Boron enhanced the formation of the 2223 phaseup to x = 0.5, gallium deteriorated one. The amount of 2223 phase was increased with increasing content of Al and In (up to x = 0.2) and then was decreased. No systematic variations of the lattice parameters with the dopant level were found. Scanning el ectron microscopy observations revealed the presence of small and irregular amounts of Ga and In in the chemical composition of superconducting grains and the existence of the various non-superconducting phases.

Název v anglickém jazyce

Influence of B, Al, Ga, In on Composition of Bi(Pb)SrCaCuO System

Popis výsledku anglicky

Samples Bi1.8-xAxPb0.26Sr2Ca2Cu3Oy were prepared to systematically examine phase formation due to concentrations x = 0 - 0.5 of B, Al, Ga and In in the range. All samples were mixed phases of 2212 and 2223. Boron enhanced the formation of the 2223 phaseup to x = 0.5, gallium deteriorated one. The amount of 2223 phase was increased with increasing content of Al and In (up to x = 0.2) and then was decreased. No systematic variations of the lattice parameters with the dopant level were found. Scanning el ectron microscopy observations revealed the presence of small and irregular amounts of Ga and In in the chemical composition of superconducting grains and the existence of the various non-superconducting phases.

Druh

D - Stať ve sborníku

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proc. Conf. on Magnetic and Superconducting Material

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

79-80

Název nakladatele

neznámý

Místo vydání

Irbid, Jordánsko

Místo konání akce

Irbid, Jordánsko

Datum konání akce

1. 1. 2001

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—