Micro-Raman studies on 50 keV electron irradiated silicate glass

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F06%3A00016926" target="_blank" >RIV/60461373:22310/06:00016926 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Micro-Raman studies on 50 keV electron irradiated silicate glass

Popis výsledku v původním jazyce

A potassium?lime-silicate glass was irradiated with a 50 keV electron beam. The impact of irradiation conditions on the glass structure (beam diameter, current, and irradiation time) was studied by Micro-Raman spectroscopy. For irradiation time less thanthe incubation time (around 360 s), structural evolutions are attributed to a glass densification. Irradiations longer than the incubation period led to a precipitation of supposed calcium enriched phase and formation of a more depolymerized silicate phase. A non-homogeneous irradiated glass structure was observed with the existence of an area (along the electron beam border) composed by a mixture of a concentrated Ca phase diluted into the amorphous silicate phase

Název v anglickém jazyce

Micro-Raman studies on 50 keV electron irradiated silicate glass

Popis výsledku anglicky

A potassium?lime-silicate glass was irradiated with a 50 keV electron beam. The impact of irradiation conditions on the glass structure (beam diameter, current, and irradiation time) was studied by Micro-Raman spectroscopy. For irradiation time less thanthe incubation time (around 360 s), structural evolutions are attributed to a glass densification. Irradiations longer than the incubation period led to a precipitation of supposed calcium enriched phase and formation of a more depolymerized silicate phase. A non-homogeneous irradiated glass structure was observed with the existence of an area (along the electron beam border) composed by a mixture of a concentrated Ca phase diluted into the amorphous silicate phase

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F06%2F0202" target="_blank" >GA104/06/0202: Změny struktury a vlastností povrchu silikátových skel ozářených elektrony</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Non-crystalline Solids

ISSN

0022-3093

e-ISSN

—

Svazek periodika

352

Číslo periodika v rámci svazku

50-51

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000242565100014

EID výsledku v databázi Scopus

—