Bismutové supravodiče dopované nanočásticemi stříbra

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F06%3A00016963" target="_blank" >RIV/60461373:22310/06:00016963 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Bi-based superconductors with nanosized silver dopant

Popis výsledku v původním jazyce

The effect of nanosized silver on formation and transport properties of Bi-2223 phase was studied. Samples with nominal composition Bi3.2Pb0.8Sr4Ca5Cu7Ox were prepared by solid state synthesis. Ag as additive was used in three different weight percentage5, 10 and 15. Ag powder was added to the initial mixture or after second calcination. All samples have critical temperature Tc in the range 108-109 K. An increase of the Bi-2223 phase content was observed at Ag concentration 10 wt%. Prolonged sinteringtime (400 h) improved critical current density Jc(77) above the value of the undoped sample. The values of porosity and density of the long sintered samples demonstrated their densification. The SEM micrographs have shown that addition of the silver improves the connectivity between the grains.

Název v anglickém jazyce

Bi-based superconductors with nanosized silver dopant

Popis výsledku anglicky

The effect of nanosized silver on formation and transport properties of Bi-2223 phase was studied. Samples with nominal composition Bi3.2Pb0.8Sr4Ca5Cu7Ox were prepared by solid state synthesis. Ag as additive was used in three different weight percentage5, 10 and 15. Ag powder was added to the initial mixture or after second calcination. All samples have critical temperature Tc in the range 108-109 K. An increase of the Bi-2223 phase content was observed at Ag concentration 10 wt%. Prolonged sinteringtime (400 h) improved critical current density Jc(77) above the value of the undoped sample. The values of porosity and density of the long sintered samples demonstrated their densification. The SEM micrographs have shown that addition of the silver improves the connectivity between the grains.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA203%2F05%2F0114" target="_blank" >GA203/05/0114: Bismutové supravodiče s nanočásticemi dopantů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physica Status Solidi (c)

ISSN

1610-1634

e-ISSN

—

Svazek periodika

3

Číslo periodika v rámci svazku

9

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

4

Strana od-do

3027-3030

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—