Cathodic behavior of malybdenum electrode in various glass melts

Popis výsledku v původním jazyce

The cathodic behavior od molybdenum electrode has been investigated in model glass melt of the basic composition of 16Na2O, 10CaO, 74SiO2 (wt.%) with additions of SO3 or Sb2O3 or without additions at 1400°C. There exists a range of cathodic potentials reduced by some hundreds milivolts against the rest state where the reduction of electroactive species acting as depolarizers of molybdenum corrosion may be suppressed. The potentials of the maximum suppression of lead or antimony precipitation correspondto potentials at which the anodic molybdenum oxidation finishes. The layers of molybdenum silicides have been not found on electrode at those potentials.

Název v anglickém jazyce

Cathodic behavior of malybdenum electrode in various glass melts

Popis výsledku anglicky

The cathodic behavior od molybdenum electrode has been investigated in model glass melt of the basic composition of 16Na2O, 10CaO, 74SiO2 (wt.%) with additions of SO3 or Sb2O3 or without additions at 1400°C. There exists a range of cathodic potentials reduced by some hundreds milivolts against the rest state where the reduction of electroactive species acting as depolarizers of molybdenum corrosion may be suppressed. The potentials of the maximum suppression of lead or antimony precipitation correspondto potentials at which the anodic molybdenum oxidation finishes. The layers of molybdenum silicides have been not found on electrode at those potentials.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics-Silikáty

ISSN

0862-5468

e-ISSN

—

Svazek periodika

50

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

7

Strana od-do

32-38

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—