Příprava a charakterizace analzimových prášků analýzami RTG a SEM

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F07%3A00018018" target="_blank" >RIV/60461373:22310/07:00018018 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61388980:_____/07:00097417 RIV/61388980:_____/07:00339524

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and characterization of analcime powders by X-ray and SEM analyses

Popis výsledku v původním jazyce

Analcime powders having controlled particle size distribution were designed as a potential precursor for the fabrication of leucite dental ceramics retaining high fracture toughness and the thermal expansion coefficient adjusted those of metals. The purpose of this study is to investigate the synthesis of analcime and the effect of principal factors influencing its crystallisation. Analcime powders were prepared by hydrothermal synthesis in a teflon-lined stainless steel autoclave. The role of the reactiove mixture, reaction temperature and time were studied. Prepared analcime was in form of homogenous powders with the uniform particle size at intervals 0.001-0.005mm depending on process parameters.

Název v anglickém jazyce

Preparation and characterization of analcime powders by X-ray and SEM analyses

Popis výsledku anglicky

Analcime powders having controlled particle size distribution were designed as a potential precursor for the fabrication of leucite dental ceramics retaining high fracture toughness and the thermal expansion coefficient adjusted those of metals. The purpose of this study is to investigate the synthesis of analcime and the effect of principal factors influencing its crystallisation. Analcime powders were prepared by hydrothermal synthesis in a teflon-lined stainless steel autoclave. The role of the reactiove mixture, reaction temperature and time were studied. Prepared analcime was in form of homogenous powders with the uniform particle size at intervals 0.001-0.005mm depending on process parameters.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/2A-1TP1%2F063" target="_blank" >2A-1TP1/063: Nové skelné a keramické materiály a pokročilé postupy jejich příprav a výrob.</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics-Silikáty

ISSN

0862-5468

e-ISSN

—

Svazek periodika

51

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

9-14

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—